通过模拟高炉内部钒氧化物发生还原的三个主要反应区,并运用相关热力学计算,分别研究影响高炉块状带、软熔滴落带及炉缸钒氧化物还原的各种因素.研究结果表明:炉料还原性能的提高有利于钒在块状带的还原;软熔滴落带温度的升高、初渣中FeO量的降低都有利钒的还原;炉缸温度应维持在1 450℃以上,渣铁间V的反应有利于提高铁水V的收得率;硅与钒氧化物的耦合反应,不仅可促进钒氧化物的还原,而且可以降低生铁含硅量.

In order to determine factors influencing the lumpy zone,soft melting and dropping zone and reduction of vanadium oxide in hearth in blast furnace,a simulation experiment on reduction of vanadium oxide has been performed in combination of thermodynamic calculation.The results prove that improving reduction performance of furnace burden favors reduction of vanadium oxides in the lumpy zone.The increase of temperature in soft melting and dropping zone and decrease of FeO content in early slag are beneficial for reduction of vanadium.The temperature of hearth should remain above 1 450 ℃,and reaction between slag and iron benefits to improve yield rate of V in molten iron.Reduction reaction between silicon and vanadium oxide not only promote reduction of vanadium,but also reduces silicon content of iron liquid.

参考文献

[1] 宁兴龙.未来新金属材料(下)[J].金属世界,2000(02):2-3.
[2] Wang Sijing;Sun Shiguo.Mining slope engineering in China[J].Engineer and Mining Journal,2000(07):13-14.
[3] 韩秀丽,王海峰,刘丽娜,姚明艳,王艳红.碱度对钒钛烧结矿显微结构的影响[J].钢铁钒钛,2009(03):56-60.
[4] 严嘉荣 .高炉冶炼钒钛磁铁矿过程中钒还原特征研究[D].重庆大学,2013.
[5] 张建廷,陈碧.攀西钒钛磁铁矿主要元素赋存状态及回收利用[J].矿产保护与利用,2008(05):38-41.
[6] Fan Xiaohui;Wang Qiang.Research on sintering properties of vanadium-titanumagnetite concentrates[A].TMS,2012:299-306.
[7] 王永红 .高炉冶炼钒钛磁铁矿钒还原机理研究[D].重庆大学,2010.
[8] 蔡保旺,胡宾生,赵华杰,郭海涛,刘巨江.钒在高炉炉渣中还原过程的研究[J].河北冶金,2012(01):10-12.
[9] 黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2006
[10] 施月循.高炉内钒还原行为的研究[M].北京:冶金工业出版社,2000:60-65.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%