研究了建筑结构用钢Q420GJC热轧及正火后的组织、性能及Nb、V析出物变化.采用电解法对热轧和正火后钢板进行Nb、V的析出物定量分析,在透射电子显微镜下进行析出物观察,结果表明,钢板正火后强度下降明显;热轧钢板厚度方向不同部位V的析出量差别不大,约为加入数量的30％,正火不能有效提高低氮钢中V的析出量,热轧态钢板中Nb的析出量从厚钢板表层到心部递增,空冷后钢板中Nb的析出量大于控冷后Nb的析出量;正火后Nb的析出量稍高于热轧.
The microstructure and mechanical properties and Nb,V precipitations of Q420GJ steel plate for construction was investigated after hot rolling and normalizing.Quantitative analysis of Nb,V precipitates had been performed by electrolytic method for hot rolled and normalized steel plates,the precipitates were observed under transmission electron microscope.Tensile tests indicated that strengths of the steel plate after normalizing remarkable decreased.TEM observation showed there was no visible difference in vanadium precipitation through thickness direction of the plate after hot rolling,and about 30％ of total added vanadium precipated.Normalizing process could not effectively improve vanadium precipitation in low nitrogen steels.Niobium precipitation increased from the surface to the centre of the as-hot rolled plate,the amount of precipitated niobium after air cooling is larger than that after controlled cooling.The amount of precipitated niobium after normalizing was somewhat higher than that of as-hot rolling.
参考文献
| [1] | 唐帅,刘振宇,王国栋,何元春.高层建筑用钢板的生产现状及发展趋势[J].钢铁研究学报,2010(10):1-6,11. |
| [2] | 文超,胡晓萍,李自钢,金学军.高性能建筑用钢的开发展望[J].热加工工艺,2008(22):103-106. |
| [3] | 王有铭;李曼云;韦光.钢材的控制轧制及控制冷却[M].北京:冶金工业出版社,2010:52-55. |
| [4] | 王祖滨;东涛.低合金高强度钢[M].北京:原子能出版社,1996:35-40. |
| [5] | 王根矶,杜海军,赵德文,刘相华.Q390低合金高强钢厚板热处理工艺[J].金属热处理,2009(07):85-89. |
| [6] | 韩孝永.铌、钒、钛在微合金钢中的作用[J].宽厚板,2006(01):39-41. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%