对冀东磁铁精粉球团矿的矿相结构进行了系统的研究.结果显示,冀东磁铁精粉焙烧球团矿的主晶相是赤铁矿,焙烧制度和预热制度都影响球团矿的显微特征,当球团矿预热温度950～1 000℃、预热时间20 min时,球团中Fe3O4基本完全氧化,Fe2O3再结晶明显,晶粒开始凝聚.当焙烧温度在1 300℃以上时球团矿有分解型Fe3O4出现,所以焙烧温度应选择在1 300℃以下较为合适.在焙烧温度1 250～1 275℃、焙烧时间大于20 min条件下,球团的抗压强度大于2 000 N/个.
The mineralogical structure of Jidong magnetite pellets was systematically studied.The results indicated that main crystal phase of Jidong magnetite pellets was hematite,and both roasting and preheating process imposed effect on the microscopic characteristics of the pellets.When preheat temperature is between 950 ℃ to 1 000 ℃ and the preheating time is 20 rin,Fe3O4 in pellets has been substantially oxidized,and Fe2O3 significantly recrystallized and grain begun to gather.When the roasting temperature excesses 1 300 ℃ Fe3O4 in pellets began decomposition.,which implies suitable roasting temperature lower than 1 300 ℃.The combination of roasting temperature at 1 250 ～ 1 275 ℃ and roasting time longer than 20 min.produce Jidong pellets with compressive strength greater than 2 000 N per.pellet.
参考文献
| [1] | 周翔,郜学.我国球团工业发展现状及趋势分析[J].冶金经济与管理,2010(06):16-18. |
| [2] | 黄柱成,张元波,陈耀铭,庄剑鸣.以赤铁矿为主配加磁铁矿制备的氧化球团矿显微结构[J].中南工业大学学报(自然科学版),2003(06):606-610. |
| [3] | 郑红霞,汪琦,潘喜峰.磁铁矿球团氧化机理的研究[J].烧结球团,2003(05):13-16. |
| [4] | 朱德庆,潘润润,姜涛,郭宇峰,杨永斌,邱冠周.酸性护炉球团矿焙烧工艺及固结机理[J].中南工业大学学报(自然科学版),2000(06):490-492. |
| [5] | 吕庆,亢立明,刘曙光,孙丽芬.冀东磁铁精矿球团焙烧机理的研究[J].钢铁研究,2008(01):9-12. |
| [6] | 李强,陈铁军,马浩,黄献宝.用球团返粉压团焙烧制备氧化球团的研究[J].烧结球团,2013(03):22-26,59. |
| [7] | 陈耀明,张元波.氧化球团矿结晶规律的研究[J].钢铁研究,2005(03):10-12. |
| [8] | 方觉,龚瑞娟,赵立树,孟辉.球团矿氧化焙烧及还原过程中的强度变化[J].钢铁,2007(02):11-13,27. |
| [9] | 潘钊彬,郭占成,荣哲.球团矿不同气氛下的高温抗压强度[J].北京科技大学学报,2011(10):1209-1213. |
| [10] | 陈耀明,李建.氧化球团矿中Fe2O3的结晶规律[J].中南大学学报（自然科学版）,2007(01):70-73. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%