研究了自制钛可溶阳极TiCxOy(x≈0.50,y≈0.50)在简单氯化物(NaCl-KCl)熔盐体系、低价钛离子浓度为3.5％的(NaCl-KCl-TiClx)熔盐体系中的电化学溶解行为,同时考察了相应体系下的阴极行为.结果表明,在上述两种熔盐体系中,阳极TiCxOy(x≈0.50,y≈0.50)均能发生电化学溶解.在简单氯化物熔盐体系中不利于得到阴极产物;在含低价钛离子的熔盐体系中有利于阴极产物的稳定得到,阳极的电流效率能够稳定在50％以上(以三价钛放电计算),阳极的溶解率从简单氯化物(NaCl-KCl)熔盐体系中的80％左右下降到50％.
参考文献
| [1] | 莫畏;邓国珠;罗方承.钛冶金[M].北京:冶金工业出版社,1998:47. |
| [2] | Wainer E .Cell feed material for the production of titanium[P].USA,2868703,1959. |
| [3] | Wainer E;Heights C;Assignor O .Production of titanium[P].USA,2722509,1955. |
| [4] | Hashimoto Y;Uriya K;Kono R .Electrowinning of titanium from its oxide.Patr 1 Fused salt electrolysis at temperatures above the melting point of the metal[J].Denkikaguku,1971,39:516-522. |
| [5] | Hashimoto Y .Electrowinning of titanium from its oxide.Patr 2 Influences of fluoride salt baths on fused-salt electrodeposition of titanium metal from dioxide[J].Denkikaguku,1971,39:938-943. |
| [6] | Hashimoto Y .Electrowinning of titanium from its oxide.Patr 3 Electrowinning taitanium from titanium dioxide or calcium titanate in calcium fluoride-magnesium fluoride molten salt baths[J].Denkikaguku,1972,40:39-44. |
| [7] | 朱鸿民;焦树强;顾学范 .一氧化钛/碳化钛可溶性固溶体阳极电解生产纯钛的方法[P].中国,CN1712571,2005. |
| [8] | 朱福兴,邓斌,秦庆东,王芳平.真空碳热还原制备碳氧钛的动力学研究[J].有色金属（冶炼部分）,2014(03):46-50. |
| [9] | 周玉昌.配碳比对TiO2真空碳热还原的影响[J].钢铁钒钛,2012(06):6-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%