为了深入研究杂质元素对硅钢成品电磁性能的影响,结合工业化生产的0.25％ Si无取向硅钢,探讨了C、S、O、N、Nb、V、Ti杂质元素总量分别为83×10-6和105×10-6时,硅钢成品的夹杂物、显微组织及电磁性能变化.结果表明,杂质元素总量会直接影响夹杂物的种类、形貌、数量和尺寸.随杂质元素总量的升高,在0～0.2 μm尺寸范围内,单个的、椭球形的MnS、CuxS夹杂物数量明显增多,两者分别为1 679× 104个/mm3和2 661×104个/mm3.这种细小的夹杂物会不同程度的劣化SRA前后硅钢成品的磁感,然后是SRA前硅钢成品的铁损,对SRA后硅钢成品的铁损则影响不大.随着连退温度的升高,杂质元素总量对SRA前硅钢成品的铁损影响差异逐渐缩小为零.
参考文献
| [1] | Nakayama T;Honjou N;Minaga T .Effects of manganese and sulfur contents and slab reheating temperatures on the magnetic properties of non-oriented semi-processed dectrical steel sheet[J].Journal of Magnetism and Magnetic Materials,2001,234:55-61. |
| [2] | Irie T;Matsumura K;Nakamura H .Development of a new non-oriented silicon steel with higher premeablity and lower core loss[J].Kawashiki Steel Giho,1978,10(1):15-22. |
| [3] | Yoshihiko Oda;Yasushi Tanaka;Nobuo Yamagami;Atsushi Chino;Katsumi Yamada .Ultra-low Sulfur Non-oriented Electrical Steel Sheets for Highly Efficient Motors: NKB-CORE[J].NKK Technical Review,2002(87):12-18. |
| [4] | 张峰,朱诚意,缪乐德,李光强.国内外高牌号无取向硅钢夹杂物的控制效果与评价[J].冶金分析,2012(07):12-20. |
| [5] | Yano K;Honda A;Obara T et al.Non-oriented silicon steel sheet and method:[P].United States,5676771,1997-10-14. |
| [6] | 吕学钧,张峰,王波,朱诚意,李光强.夹杂物对无取向硅钢磁性能的影响[J].特殊钢,2012(04):22-25. |
| [7] | 李永超,李娜,岳尔斌,项利,张延玲,仇圣桃.高效电机用无取向硅钢退火板组织和析出物研究[J].钢铁钒钛,2011(04):71-75. |
| [8] | 马红旭,李友国.硅钢中析出物的尺寸分布以及体积分数的测定[J].材料科学与工程,2002(03):328-330,389. |
| [9] | 何忠治;赵宇;罗海文.电工钢[M].北京:冶金工业出版社,2012 |
| [10] | 金自力,任慧平,张红杰.无取向硅钢退火织构的演变与磁性能关系的研究[J].材料热处理学报,2007(02):77-80. |
| [11] | 金自力,任慧平,王玉峰,李文学,杨慧.冷轧无取向硅钢的织构和组织性能分析[J].特殊钢,2004(01):32-33. |
| [12] | 贾旭,陈晓.残余应力及去应力退火对无取向电工钢性能的影响[J].世界钢铁,2009(04):57-61. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%