以沥青作为添加剂,开展了一次烧结成型制备碳氧钛可溶阳极探索试验,研究该种可溶阳极在NaCl-KCl-TiClx熔盐体系中的电化学溶解行为.结果表明:在较优的工艺条件下,制备的一次烧结成型可溶阳极密度为1.3～1.4 g/cm3,摔落强度符合电解要求;一次烧结成型可溶阳极在低价钛(NaCl-KCl-TiClx)熔盐体系中能实现稳定电化学溶解.
Titanium oxycarbid consumable anode was prepared by single sintering process with asphalt as additive agent.Electrochemical dissolution behaviors of titanium oxycarbid consumable anode in NaCl-KCl-TiClx molten salt system was researched.The results show that titanium oxycarbid consumable anode with 1.3 g/cm3 ～ 1.4 g/cm3 of density and strength meeting the requirements of the electrolytic process can be obtained under the optimal conditions.The consumable anode prepared by single sintering process can normally dissolve in the molten salt systems.