采用光学显微镜、扫描电子显微镜、X射线衍射仪及腐蚀质量损失试验、电化学腐蚀试验,研究铸态和挤压态Mg992Ca0.6Mn02合金(原子数分数)在SBF溶液中的腐蚀行为及腐蚀性能.结果表明:Mg992Ca06Mn02合金的腐蚀速率随着时间的延长而降低；挤压可显著提高合金的耐蚀性.经过11d浸泡后,铸态合金的平均腐蚀速率从最初的15.43 mm/a下降到8.64 mm/a,挤压态合金的平均腐蚀速率从10.68 mm/a下降到3.79 mm/a.挤压态合金的瞬时腐蚀速率为4.070 9 mm/a,比铸态降低33.3％.铸态Mg992Ca06Mn02合金在SBF溶液腐蚀的过程中产生氢气和Mg(OH)2沉淀,Mg(OH)2疏松多孔,不能对合金起到很好的保护作用.
参考文献
| [1] | Staiger MP;Pietak AM;Huadmai J;Dias G .Magnesium and its alloys as orthopedic biomaterials: A review[J].Biomaterials,2006(9):1728-1734. |
| [2] | 黎文献.镁及镁合金[M].长沙:中南大学出版社,2005:501-503. |
| [3] | Kannan MB;Raman RKS .In vitro degradation and mechanical integrity of calcium-containing magnesium alloys in modified-simulated body fluid[J].Biomaterials,2008(15):2306-2314. |
| [4] | Heublein B;Rohde R;Kaese V et al.Biocorrosion of magnesium alloys:a new principle in cardiovascular implant technology[J].Heart,2003,89(06):651-656. |
| [5] | 尹冬松,张二林,曾松岩.挤压对Mg-Mn-Zn合金力学性能和腐蚀行为的影响[J].材料热处理学报,2009(01):114-118. |
| [6] | Li Z;Gu X;Lou S;Zheng Y .The development of binary Mg-Ca alloys for use as biodegradable materials within bone.[J].Biomaterials,2008(10):1329-1344. |
| [7] | YeoHeung Yun;Zhongyun Dong;Dianer Yang;Mark J. Schulz;Vesselin N. Shanov;Sergey Yarmolenko;Zhigang Xu;Prashant Kumta;Charles Sfeir .Biodegradable Mg corrosion and osteoblast cell culture studies[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2009(6):1814-1821. |
| [8] | 高家诚,李龙川,王勇.镁表面改性及其在仿生体液中的耐蚀行为[J].中国有色金属学报,2004(09):1508-1513. |
| [9] | 许鑫华,程静,张春怀,闫学良,朱天兵,姚康德,曹路,刘寅.医用镁合金的生物腐蚀及高分子涂层处理[J].稀有金属材料与工程,2008(07):1225-1228. |
| [10] | 任伊宾,黄晶晶,杨柯,张炳春,姚治铭,王浩.纯镁的生物腐蚀研究[J].金属学报,2005(11):1228-1232. |
| [11] | Kokubo T;Takadama H .How useful is SBF in predicting in vivo bone bioactivity?[J].Biomaterials,2006(15):2907-2915. |
| [12] | 欧阳春,雷霆,王丽,李年丰,周乐山.Mg-Zn-Ca三元镁合金生物材料的腐蚀行为[J].中国有色金属学报,2010(05):891-897. |