通过扫描电镜、透射电镜和EDS分析,对残余元素对连铸坯和热轧板表面质量的影响进行了研究.试验结果表明,连铸坯氧化层中存在铜、砷和锡同时富集.热轧板基体层与氧化层界面存在铜、砷和锡富集,基体层铜、砷和锡含量高于氧化层铜、砷和锡含量.铜、砷和锡在γ晶界偏聚和铁优先氧化造成连铸坯中铜、砷和锡富集,加热炉二次加热加剧铜、砷和锡富集,铜、砷、锡向钢基体渗透扩散,恶化钢的塑性,导致中板表面微裂纹缺陷,分析了铜、砷和锡富集相对表面微裂纹的影响机理.
参考文献
| [1] | Hartman A D;Oden L L;Davis D L.Copper Removal From Solid Ferrous Scrap by a Solid/Gas Reaction[J].Iron and Steelmaker,1994(05):59. |
| [2] | 王中丙,谢利群,柴毅忠.CSP生产的热轧薄板边裂的影响因素与控制[J].钢铁,2002(09):31-34. |
| [3] | Iwase M;Tokinori K;Ohshita H.Separation of Copper From Solid Ferrous Scrap by Using Molten Aluminum[J].Iron and Steelmaker,1993(07):61. |
| [4] | J. C. Herman .Influence of residual elements on steel processing and mechanical properties[J].Iron & Steelmaker,1996(12):35-43. |
| [5] | 梶谷敏之;若生昌光;德光直樹 .Cuによる炭素鋼の脆化に及ほす温度と歪の影響[J].鉄と鋼,1995,81(03):185. |
| [6] | 张翔,刘旭辉.高强度船板钢裂纹产生原因探讨[J].钢铁,2001(11):46-49. |
| [7] | N.Imai .Effect of Cu, Sn and Ni on Hot Workability of Hot-rolled Mild Steel[J].ISIJ International,1997(3):217-223. |
| [8] | H.Ohtani .Solid/Liquid Equilibria in Fe-Cu Based Ternary Systems[J].ISIJ International,1997(3):207-216. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%