An N38SH-grade magnet with low oxygen content was used to study the evolution of magnetic properties upon post-sin-tering annealing. Phase transformation of as-sintered magnet was investigated by differential scanning calorimetry (DSC). Three low temperature eutectic transition points were detected. Little change could be found when annealed below the lowest eutectic transition point. A wide annealing temperature range (460–560 oC) between the lowest and highest eutectic transition point was available for this magnet to achieve a relatively high coercivity (~1671 kA/m) at a relatively low Dy content (~3 wt.%). However, squareness fac-tor (SF) of the demagnetizing curve and its temperature stability were found to decrease after annealing above the highest eutectic transition point. This was attributed to the change of Cu content in the Nd-rich phase under different annealing temperatures.
参考文献
| [1] | Gutfleisch O, Willard M A, Bruck E, Chen C H, Sankar S G, Liu J P. Magnetic materials and devices for the 21st century:stronger, lighter, and more energy efficient. Adv. Mater., 2011, 23(7):821.,2011. |
| [2] | Hono K, Sepehri-Amin H. Strategy for high-coercivity Nd-Fe-B magnets. Scripta Mater., 2012, 67(6):530.,2012. |
| [3] | Woodcock T G, Zhang Y, Hrkac G, Ciuta G, Dempsey N M, Schrefl T, Gutfleisch O, Givord D. Understanding the microstructure and coercivity of high performance NdFeB-based magnets. Scripta Mater., 2012, 67(6):536.,2012. |
| [4] | Zhou S, Dong Q. Super Permanent Magnets:Rare Earth Iron Based Permanent Materials(in Chin.). Beijing:Met-allurgy Industry Press, 2004.,2004. |
| [5] | Li W F, Ohkubo T, Hono K. Effect of post-sinter anneal-ing on the coercivity and microstructure of Nd-Fe-B per-manent magnets. Acta Mater., 2009, 57(5):1337.,2009. |
| [6] | Pi S H, Choi J M, Kim Y G. Effects of heat treatments on coercivity and microstructure in Nd15Fe77B8 sintered mag-nets. Mater. Sci. Eng. B, 1995, 32:89.,1995. |
| [7] | Sepehri-Amin H, Ohkubo T, Shima T, Hono K. Grain boundary and interface chemistry of an Nd-Fe-B-based sintered magnet. Acta Mater., 2012, 60(3):819.,2012. |
| [8] | Vial F, Joly F, Nevalainen E, Sagawa M, Hiraga K, Park K T. Improvement of coercivity of sintered NdFeB perma-nent magnets by heat treatment. J. Magn. Magn. Mater., 2002, 242-245:1329.,2002. |
| [9] | Yan M, Yu L Q, Luo W, Wang W, Zhang W Y, Wen Y H. Change of microstructure and magnetic properties of sin-tered Nd-Fe-B induced by annealing. J. Magn. Magn. Ma-ter., 2006, 301(1):1.,2006. |
| [10] | Mishra R K, Chen J K, Thomas G. Effect of annealing on the microstructure of sintered Nd-Fe-B magnets. J. Appl. Phys., 1986, 59(6):2244.,1986. |
| [11] | Ramesh R. A microstructure based magnetization reversal model in sintered Fe-Nd-B magnets. II. Effect of post sin-tering treatments. J. Appl. Phys., 1990, 68(11):5772.,1990. |
| [12] | Fidler J, Bernardi J. Transmission electron microscope characterization of cast and hot-worked R-Fe-B:Cu(R=Nd,Pr)permanent magnets. J. Appl. Phys., 1991, 70(10):6456.,1991. |
| [13] | Cui X G, Yan M, Ma T Y, Yu L Q. Effects of Cu nano-powders addition on magnetic properties and corrosion re-sistance of sintered Nd-Fe-B magnets. Physica B, 2008, 403(23-24):4182.,2008. |
| [14] | Knoch K G, Schneider G, Fidler J, Henig E-T, Kronmuller H. Al-doped Nd-Fe-B permanent magnets wetting and microstructural investigations. IEEE Trans. Magn., 1989, 25(5):3426.,1989. |
| [15] | Akiya T, Sasaki T T, Ohkubo T, Une Y, Sagawa M, Kato H, Hono K. The origin of the coercivity reduction of Nd-Fe-B sintered magnet annealed below an optimal tem-perature. J. Magn. Magn. Mater., 2013, 342:4.,2013. |
| [16] | Kianvash A. Effect of post-sintring annealing treatment on magnetic properties of some NdFeB based magnets. Int. J. Eng. Trans. B, 2002, 15(1):87.,2002. |
| [17] | Liu Q Z, Xu F, Wang J, Dong X P, Zhang L T, Yang J Y. An investigation of the microstructure in the grain bound-ary region of Nd-Fe-B sintered magnet during post-sin-tering annealing. Scripta Mater., 2013, 68(9):687.,2013. |
| [18] | Shinba Y, Konno T J, Ishikawa K, Hiraga K, Sagawa M. Transmission electron microscopy study on Nd-rich phase and grain boundary structure of Nd-Fe-B sintered magnets. J. Appl. Phys., 2005, 97(5):053504.,2005. |
| [19] | 付新,韩小磊,杜志伟,冯海波,李岩峰.Microstructural investigation of Nd-rich phase in sintered Nd-Fe-B magnets through electron microscopy[J].稀土学报（英文版）,2013(08):765-771. |
| [20] | Mo W J, Zhang L T, Liu Q Z, Shan A D, Wu J S, Komuro M. Dependence of the crystal structure of the Nd-rich phase on oxygen content in an Nd-Fe-B sintered magnet. ScriptaMater., 2008, 59(2):179.,2008. |
| [21] | Yi G, Chapman J N, Brown D N, Harris I R. TEM studies of the effects of Zr additions on some HDDR-processed high boron NdFeB-type powders and hot-pressed magnets. J. Magn. Magn. Mater., 2000, 220:115.,2000. |
| [22] | Sepehri-Amin H, Ohkubo T, Hono K. Grain boundary structure and chemistry of Dy-diffusion processed Nd-Fe-B sintered magnets. J. Appl. Phys., 2010, 107(9):09A745.,2010. |
| [23] | Hu Z H, Lian F Z, Zhu M G, Li W. Effect of Co on the thermal stability and impact toughness of sintered Nd-Fe-B magnets. J. Magn. Magn. Mater., 2008, 320(19):2364.,2008. |
| [24] | Oono N, Sagawa M, Kasada R, Matsui H, Kimura A. Pro-duction of thick high-performance sintered neodymium magnets by grain boundary diffusion treatment with dys-prosium-nickel-aluminum alloy. J. Magn. Magn. Mater., 2011, 323(3-4):297.,2011. |
| [25] | Subramanian P R, Laughlin D E. Cu-Nd(Copper-Neo-dymium). Binary Alloy Phase Diagrams, II Edn., Massal-ski T B, Ed. Vol. 2, 1990. 1442.,1990. |
| [26] | Sepehri-Amin H, Liu J, Ohkubo T, Hioki K, Hattori A, Hono K. Enhancement of coercivity of hot-deformed Nd-Fe-B anisotropic magnet by low-temperature grain boundary diffusion of Nd60Dy20Cu20 eutectic alloy. Scripta Mater., 2013, 69(9):647.,2013. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%