用预处理的铝箔,以草酸为电解液,采用二步阳极氧化法制备多孔有序阳极氧化铝阵列模板,利用透射电镜和X射线衍射仪对其进行表征,并对阵列孔的形成机理进行分析.结果表明:适当提高电压有利于孔的有序化;孔的有序化存在一个最佳阳极氧化时间,本试验条件下为6 h;根据试验结果并结合目前几个常见模型可较圆满解释阵列孔的形成过程.
参考文献
| [1] | Martin C R .Nanomatrials:A membrane based synthetic approach[J].Science,1994,266:1961-1966. |
| [2] | 张立德.纳米材料学[M].沈阳:辽宁科学技术出版社,1994 |
| [3] | 姚素薇,孔亚西,张璐.高度有序多孔阳极氧化铝膜形成机理的探讨[J].功能材料,2006(01):113-116. |
| [4] | 江小雪,赵乃勤.多孔氧化铝膜的制备与形成机理的研究概况[J].功能材料,2005(04):487-489,494. |
| [5] | Jessensky O.;Gosele U.;Muller F. .Self-organized formation of hexagonal pore arrays in anodic alumina[J].Applied physics letters,1998(10):1173-1175. |
| [6] | Sullivan J P;Wood G C .The morphology and mechanism of formation of porous anodic films on aluminum[J].Proceedings of the Royal Society of London Series A:Mathematical and Physical Sciences,1970,317:511-543. |
| [7] | Xu Y;Thompson G E;Wood G C .Mechanism of anodic film growth on aluminum[J].Trans Transactions of the Institute of Metal Finishing,1985,63:98-103. |
| [8] | 刘海平;徐源;张文奇 .铝的壁垒型阳极氧化膜的透射电镜观察[J].北京科技大学学报,1990,12(02):77-81. |
| [9] | Parkhutik V P;Shershulsky V I .Theoretical modelling of porous oxide growth on aluminium[J].Journal of Physics D:Applied Physics,1992,25(08):1258-1263. |
| [10] | 徐源;Thompson G E;Wood G C .多孔型铝阳极氧化膜孔洞形成过程的研究[J].中国腐蚀与防护学报,1989,9(01):1-10. |
| [11] | 徐滨士.纳米表面工程[M].北京:化学工业出版社,2004 |
| [12] | 许并社.纳米材料及应用技术[M].北京:化学工业出版社,2004 |
| [13] | 王世敏;许祖勋;傅晶.纳米材料制备技术[M].北京:化学工业出版社,2001 |
| [14] | 徐金霞,黄新民,钱利华.二次阳极氧化方法制备有序多孔氧化铝膜[J].化学物理学报,2003(03):223-226. |
| [15] | 徐源;Thompson G E;Bethune B B .壁垒型铝阳极氧化膜的成分及电解质离子在膜中的漂移[J].中国腐蚀与防护学报,1987,7(03):12-21. |
| [16] | 黎樵焱 .铝阳极氧化膜的形态结构和成分分布的研究[J].表面技术,1992,21(04):17-25. |
| [17] | 余永宁.金属学原理[M].北京:冶金工业出版社,2000 |
| [18] | 魏剑,李克智,李贺军,李正佳,付前刚.多孔阳极氧化铝薄膜的制备[J].材料工程,2005(05):56-59,64. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%