以D,L-乳酸熔融聚合直接合成的低分子量聚外消旋乳酸(PDLLA)为原料,通过二异氰酸酯扩链合成聚乳酸类药物缓释材料,用2,4-甲苯二异氰酸酯(TDI)为扩链剂进行扩链的最佳工艺条件为:在SnCl2催化下,NCO/OH=1:1时,160℃下反应60min,分子量增加3.42倍,同时也提高了以乳酸为初始原料合成聚乳酸类药物缓释材料的利用率.
参考文献
| [1] | Kricheldorf HR .Syntheses and application of polylactides[J].Chemosphere,2001,43:49. |
| [2] | 陶忠华 .聚乳酸类生物降解聚合物在控释制剂中的应用[J].药学进展,1996,20(04):197. |
| [3] | Woo SI;Kim BO;Jun HS et al.Polymerization of aqueous lactic acid to prepare high molecular weight poly (lactic acid) by chain-extending with hexamethylene diisocyanate[J].POLYMER BULLETIN,1995,35(04):415. |
| [4] | 钟伟;戈进杰;马敬红 等.聚乳酸的直接缩聚制备及其异氰酸酯扩链探索[J].复旦学报(自然科学版),1999,38(06):705. |
| [5] | 汪朝阳,赵耀明,麦杭珍,严冰.熔融聚合法直接合成聚乳酸的研究[J].合成纤维,2002(02):11-13. |
| [6] | Tuominen J.;Kylma J.;Seppala J. .Chain extending of lactic acid oligomers. 2. Increase of molecular weight with 1,6-hexamethylene diisocyanate and 2,2 '-bis(2-oxazoline)[J].Polymer: The International Journal for the Science and Technology of Polymers,2002(1):3-10. |
| [7] | Vandijk J;Smit J .Characterization of poly (d, 1 -lactic acid) by gel permeation chromatography[J].Journal of Polymer Science Part A:Polymer Chemistry,1983(21):197. |
| [8] | 郝冈岭 .二异氰酸酯与二元醇反应化学[J].皮革化工,1994,2:38. |
| [9] | 方禹声;朱吕民.聚氨酯泡沫塑料[M].北京:化学工业出版社,1996 |
| [10] | 邹新伟;杨淑英;陈立班 等.生物降解型聚氨酯[J].化学世界,1997,38(09):451. |
| [11] | 杨帆,陈一岳,林茵,赵耀明,麦杭珍.聚乳酸的降解性能及其微球剂的研究[J].中国药房,2002(05):263-265. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%