在60℃时采用浸渍法制备硅烷稀土复合膜,通过先在试样表面自组装一层γ-氨丙基三乙氧基(γ-APS)硅烷薄膜,再在膜上沉积稀土铈转化膜制得硅烷稀土复合膜.采用电化学、失重和盐雾实验对铝管表面硅烷稀土复合膜的耐蚀性进行考察.线性电位扫描、Tafel曲线和交流阻抗(EIS)的结果均表明其耐蚀性与空白样相比,极化电阻和自腐蚀电流均提高了两个数量级,阻抗阻值提高了2倍;盐雾实验结果也表明其抗蚀能力提高了3倍;SEM显示其复合膜层均匀致密,EDS检测分析表明复合膜主要由N,0,Si,Al和Ce等元素组成;初步探讨了复合膜的耐蚀机制.
Silane-rare earth composite coating was prepared by impregnation method at 60 ℃. The sample with a self-assembled monolayer of γ-aminopropyhfiethoxy (γ-APS) silane was immersed in the solution with cerium to get the complex coating. Corrosion resistance of aluminum tube surface with silane-rare earth composite coating was studied by electrochemical means, weight loss and salt spray test respectively. The results of linear potential sweep, Tafel curves and electrochemical impedance spectroscopy (EIS) indicated that the polarization resistance and self-corrosion current increased by two orders of magnitude, and impedance increased by two times, the corrosion resistant capability was improved significantly. The results of salt spray test showed that the anti-corrosion time increased by three times; Scanning electron microscope (SEM) observation showed that the composite coating was uniform and dense; X-ray en-ergy dispersive spectroscopy (EDS) test showed that the composite coating was mainly composed of N, O, Si, Al and Ce. The corro-sion protection mechanism of the composite coating was analyzed.
参考文献
| [1] | Arnott D R;Ryan N E;Hinton B B;Sexton B A Hughes A E .Auger and XPS studies of cerium corrosion inhibition on 7075 aluminuro-alloy[J].Applied Surface Science,1985,22-23:2366. |
| [2] | 陈锦虹,卢锦堂,许乔瑜,孔纲,眭润舟.镀锌层无铬钝化研究的进展[J].腐蚀科学与防护技术,2003(05):277-281. |
| [3] | Hinton B R .Corrosion inhibition with rare earth metal salts[J].Journal of Alloys and Compounds,1992,180(1-2):15. |
| [4] | Hinton B R W;Trathen P N;Wilson L.The inhibition of mild steel corrosion in tap water by cerous chloride[A].Perth,Australia,1988 |
| [5] | 张景怀,唐定骧,张洪杰,王立民,王军,孟健.稀土元素在镁合金中的作用及其应用[J].稀有金属,2008(05):659-667. |
| [6] | 王铁宝,齐向前,王晓东,刘春阳.稀土对3X04铝合金铸态组织及性能的影响[J].稀有金属,2008(04):425-428. |
| [7] | Luis E;M Palomino;Patricia H Suegama;ldalina V Aoki,Zoltan Paszti,Hercilio G de Melo .Investigation of the corrosion behaviour of a bilayer cerium-silone pre-treatment on Al,2024-T3 in 0.1M NaCl[J].Electrochimica Acta,2007,52(06):7496. |
| [8] | 刘倞,胡吉明,张鉴清,曹楚南.金属表面硅烷化防护处理及其研究现状[J].中国腐蚀与防护学报,2006(01):59-64. |
| [9] | 张明宗,管从胜,王威强.有机硅烷偶联剂在金属表面预处理中的应用[J].腐蚀科学与防护技术,2001(02):96-100. |
| [10] | 葛科 .盐酸介质中铝的腐蚀与防护研究[D].重庆大学,2007. |
| [11] | 曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994 |
| [12] | 张鉴清;曹楚南 .电化学阻抗谱方法研究评价有机涂层[J].腐蚀与防护,1998,19(03):99. |
| [13] | 徐斌,满瑞林,倪网东,胡豫,曹晓燕,颜莎,史燕.镀锌钢板表面硅烷、铈盐复合膜的制备及耐腐蚀性能研究[J].涂料工业,2007(12):46-50. |
| [14] | Scholes FH;Soste C;Hughes AE;Hardin SG;Curtis PR .The role of hydrogen peroxide in the deposition of cerium-based conversion coatings[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(4):1770-1780. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%