将钛管、钢管利用冷拔-内压扩散法制备了内包覆钛-钢复管.用扫描电镜、能谱分析、X-光衍射和拉剪试验等方法,研究了扩散退火温度与时间对钛-钢扩散复合界面附近组织、成分和界面剪切强度的影响.结果表明,该制备方法可使钛-钢实现冶金结合;界面剪切强度随扩散温度升高先增加后减小;750-800℃×0.5h扩散退火界面剪切强度最高,可达210MPa左右;扩散退火中Fe、Ti原子发生了互扩散;界面上有TiC形成;750℃×0.5 h扩散退火试样断口未检测到TiFe、TiFe2相;900-950℃×0.5h扩散退火钢侧出现柱状晶区,钛侧出现无晶界晶区与针状马氏体晶区.
参考文献
| [1] | 黄金昌.NKK开发钛钢轧制复合板[J].稀有金属快报,2002(06):3-5. |
| [2] | S. Kundu;S. Chatterjee .Effect of bonding temperature on interface microstructure and properties of titanium-304 stainless steel diffusion bonded joints with Ni interlayer[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2006(10):1201-1207. |
| [3] | M. Ghosh;A. Laik;K. Bhanumurthy;G. B. Kale;J. Krishnan;S. Chatterjee .Evolution of interface microstructure and strength properties in titanium-stainless steel diffusion bonded transition joints[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2004(12):1578-1584. |
| [4] | 彭文安.轧制钛钢复合板的新进展[J].钛工业进展,1991(05):7-9. |
| [5] | 孟杰,刘世程,刘德义,陈汝淑,戴雅康.内包覆铜钢双金属管内压扩散复合工艺研究[J].大连铁道学院学报,2002(04):79-82. |
| [6] | 刘德义,刘世程,陈汝淑,王晓峰.黄铜/钢扩散复合双金属界面组织与性能[J].材料热处理学报,2007(01):110-113. |
| [7] | 晋军辉,刘世程,陈汝淑,刘德义,戴雅康.扩散复合不锈钢/碳钢双金属管界面组织与性能[J].大连铁道学院学报,2004(01):65-68. |
| [8] | Mellesham P;Gokhale A A;Murti V S R .Nature of the interface between AA7072 alloy explosively clad to AA8090 alnminium alloy[J].Journal of Materiels Science,2003,38:1869-1873. |
| [9] | 日野谷;重晴 .純チタソと純鉄拡散接合界面の微視的構造と接合強度[J].铁と钢(日本),1989,75(09):281-288. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%