采用浸入法来模拟熔融碳酸盐燃料电池(MCFC)环境,研究了MCFC 电解质基板材料 LiAlO2在不同条件下相的穗定性.α-、β-LiAlO2在空气环境下是不稳定的;在含CO2气氛中却发现γ-和a-两相存在相互转变,说明混合体系在MCFC环境下能够保持初始相组成.
参考文献
[1] | Eiichi Yasumoto;Hatoh;Takaharu Gamo.Par ticle growth behaviour of LiAlO2 containing ZrO2 in Li/Na carbonate electrlytes[J].Journal of Power Sources,1998(71):159. |
[2] | Lacovangelo C D et al.[J].Journal of the Electrochemical Society,1988,124(01):221. |
[3] | 陈铭,温廷琏.LiAlO2粉体的合成[J].化学通报,1998(10):19-23. |
[4] | Seiji Terada;Nagashima;Kenjin Higaki et al.Stabil ity of LiAlO2 as electrolyte matrix for molten carbonate fuel cells[J].Journal of Power Sources,1998,75(02):223. |
[5] | Webb A N;Mather W B;Suggitt R M .Studies of the molten carbonates electrolyte fuel cell[J].Journal of the Electrochemical Society,1965,112(11):1059. |
[6] | Murai M.;Soejima K.;Sotouchi H.;Takizawa K. .LITHIATION OF ALUMINA IN MOLTEN LI/K CARBONATES[J].Journal of the Electrochemical Society,1996(11):3456-3462. |
[7] | 大图秀行;中川和明;富松师浩 等.MCFCC)实用化に向けこ新電解質板の开发[J].電気化学,1998,66(07):696. |
[8] | Jimenez Becerril J;Bosch P;Bulbulian S .Synthesis and characterization of LiAlO2[J].Journal of Nuclear Materials,1991,185(03):304. |
[9] | Richard Dronskowski .Reactivity and acidity of Li in LiAlO2 phases[J].Inorganic Chemistry,1993,32(01):1. |
[10] | 徐科,邓佩珍,徐军,周永宗,刘文军,蒋树声,蒋建华.两种新型衬底材料 LiAlO2和LiGaO2晶体的腐蚀形貌和缺陷研究[J].硅酸盐学报,1998(03):281-285. |
[11] | Poeppelmeier K R;C K;Kipp D O .Synthesis of high-surface-area α-LiAlO2[J].Inorganic Chemistry,1988,27(25):4523. |
[12] | Huijsmans J P P;Kraaij G J;Makkus R C et al.An ana lysis of endurance issues for MCFC[J].Journal of Power Sources,2000,86:117. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%