采用准稳态的极化试验研究了各主要试验参数对碳钢在3%NaCl溶液中点蚀电位的影响,结果表明:3种碳钢钝化的临界pH值约为8.0;当T=20℃～35℃时,点蚀电位值Eb100随温度的降低而变正;当电位变化速度慢于30 mV/30 s时,Eb100随电位变化速度的减小而变负;试验面的粗糙度越大,点蚀电位越负.
参考文献
| [1] | 上海钢铁研究所主编,保护电位在孔蚀和晶间腐蚀中的意义,国外海洋用金属材料(腐蚀机理与试验方法)[R].上海:上海科学技术情报研究所,1975.76. |
| [2] | 中国腐蚀与防护学会主编,杨武等编著.金属的局部腐蚀[M].北京:化学工业出版社,1994.13. |
| [3] | Mant H C, GABE D R. A study of pitting potentials for some austenitic stainless steels using a potentiodynamic technique[J].Corrosion Sicence, 21 (9): 713. |
| [4] | Pourbaix M. The relation of expermential potential-pH diagram of pure ferrite[J]. Corrosion, 1970, 26:431. |
| [5] | Shih H C, Hsu J, Tand Oung J C. Expermential potential- pH diagram for commercial steels in sea water[A]. International Congress on Metallic Corrosion[D], Vo1. 4, Toronto Canada,1984. 517. |
| [6] | Manning P E, Duquette D, Jand Savage W F. The effect test method and surface condition on pitting potential of single and duplex phase 304 L stainless steel [J]. Corroion, 1979, 35 (4):151. |
| [7] | 金属腐蚀试验方法[R].北京:北京科技大学,1990.248. |
| [8] | 吴继勋,金属的钝化与局部腐蚀[R].北京:北京科技大学,1993.99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%