On the basis of regular solution sublattice model, thermodynamic equilibrium of austenite/carbide in Fe-Nb-C ternary system was investigated. The equilibrium volume fraction, chemical driving force of carbide precipitates and molar fraction of niobium and carbon in solution at different temperatures were evaluated respectively. The volume fraction of precipitates increases, molar fraction of niobium dissolved in austenite decreases and molar fraction of carbon increases with decreasing the niobium content. The driving force increases with the decrease of temperature, and then comes to be stable at relatively low temperatures. The predicted ratio of carbon in precipitates is in good agreement with the measured one.

参考文献

[1] Hillert M;Jarl M A .Thermodynamic Analysis of the Iron-Nitrogen System[J].Metallurgical and Materials Transactions,1975,6A:553-558.
[2] Lakshmanan V K .Thermodynamics of the Interstitial Phases of Niobium in Iron Austenite[D].Hamilton:McMaster University,1977.
[3] Ohtani H;Hasebe M;Nishizawa T .Calculation of Fe-C,Co-C and Ni-C Phase Diagrams[J].Transactions Iron Steel Inst,1984,24:857-863.
[4] Kaufman L;Bernstein H.Computer Calculation of Phase Diagrams[M].New York:Academic Press,Inc,1970
[5] Ohtani H;Hasebe M;Nishizawa T .Calculation of Fe-C-Nb Ternary Phase Diagram[J].Calphad-computer coupling of phase diagrams and thermochemistry,1989,13:187-194.
[6] 许云波,于永梅,吴迪,王国栋.Nb微合金钢析出行为的热力学计算[J].材料研究学报,2006(01):104-108.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%