对铝合金表面经化学法、机械-化学法或化学-阳极氧化法预处理后,再经铺设玻璃纤维布、浸渍环氧树脂、静置固化等过程,获得玻璃纤维-铝合金叠层板;观察分析了铝合金表面和叠层板界面微观形貌,并测试叠层板力学特性.结果表明:3种预处理方法相比较,铝合金表面微孔孔径依次增大、孔数依次增多、分布依次更均匀;化学-阳极氧化法处理的铝合金制备的叠层板界面缺陷少、力学特性好.
参考文献
| [1] | C.M. Cepeda-Jimenez;R.C. Alderliesten;O.A. Ruano;F. Carreno .Damage Tolerance Assessment By Bend And Shear Tests Of Two Multilayer Composites: Glass Fibre Reinforced Metal Laminate And Aluminium Roll-bonded Laminate[J].Composites science and technology,2009(3/4):343-348. |
| [2] | 郑丽娟,赵玉涛,程晓农,陈志刚.仿生叠层复合材料的制备及层间性能研究[J].机械工程材料,2003(07):35-37,54. |
| [3] | 李文娟,汪浩,杨浩邈,曾庆文,彭晓东,谢卫东.温度对玻璃纤维-环氧树脂润湿性的影响[J].兵器材料科学与工程,2012(06):42-44. |
| [4] | Sang Yoon Park;Won Jong Choi;Heung Soap Choi;Hyuk Kwon .Effects of surface pre-treatment and void content on GLARE laminate process characteristics[J].Journal of Materials Processing Technology,2010(8):1008-1016. |
| [5] | Zhang JS;Zhao XH;Zuo Y;Xiong JP .The bonding strength and corrosion resistance of aluminum alloy by anodizing treatment in a phosphoric acid modified boric acid/sulfuric acid bath[J].Surface & Coatings Technology,2008(14):3149-3156. |
| [6] | E.C. Botelho;L.C. Pardini;M.C. Rezende .Hygrothermal effects on damping behavior of metal/glass fiber/epoxy hybrid composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):190-198. |
| [7] | 吴敏,孙勇.铝及其合金表面处理的研究现状[J].表面技术,2003(03):13-15. |
| [8] | 翟豹,王树彬,张博明,岳广全.阳极氧化工艺对纤维-铝合金层板力学性能的影响[J].复合材料学报,2013(03):154-159. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%