基于密度泛函理论第一性原理,在广义梯度近似下,本文研究本征石墨烯和掺杂不同浓度P的石墨烯结构和电子性质并发现本征石墨烯禁带宽度为零;对于P∶C掺杂比分别为1∶17、1∶7、1∶1的石墨烯,其P-C键长由0.142nm的C-C键分别增大为0.1629 nm、0.1625 nm、0.1751 nm,其对应带隙分别由零带隙变为0.28 eV、0.44 eV、1.21eV:费米能级逐渐下降.分析分波态密度后发现,在掺P石墨烯中主要为P原子的3p态电子影响其总态密度.
参考文献
| [1] | Jaemyung Kim;Franklin Kim;Jiaxing Huang .Seeing graphene-based sheets[J].Materials Today,2010(3):28-38. |
| [2] | Matthew J. Allen;Vincent C. Tung;Richard B. Kaner .Honeycomb Carbon: A Review of Graphene[J].Chemical Reviews,2010(1):132-145. |
| [3] | Weitz, R.T.;Yacoby, A. .Nanomaterials: Graphene rests easy[J].Nature nanotechnology,2010(10):699-700. |
| [4] | Changgu Lee;Xiaoding Wei;Jeffrey W. Kysar;James Hone .Measurement of the Elastic Properties and Intrinsic Strength of Monolayer Graphene[J].Science,2008(5887):385-388. |
| [5] | Ziegler K .Minimal conductivity of graphene: Nonuniversal values from the Kubo formula[J].Physical review, B. Condensed matter and materials physics,2007(23):3407-1-3407-4-0. |
| [6] | Nair RR;Blake P;Grigorenko AN;Novoselov KS;Booth TJ;Stauber T;Peres NM;Geim AK .Fine structure constant defines visual transparency of graphene.[J].Science,2008(5881):1308-1308. |
| [7] | 邹志宇,戴博雅,刘忠范.石墨烯的化学气相沉积生长与过程工程学研究[J].中国科学（化学）,2013(01):1-17. |
| [8] | Weatherup, R.S.;Bayer, B.C.;Blume, R.;Ducati, C.;Baehtz, C.;Schl?gl, R.;Hofmann, S. .In situ characterization of alloy catalysts for Low-temperature graphene growth[J].Nano letters,2011(10):4154-4160. |
| [9] | 孙雷,沈鸿烈,吴天如,刘斌,蒋烨.抛光铜箔衬底上石墨烯可控生长的研究[J].人工晶体学报,2012(02):407-413. |
| [10] | 赵琰,毕见强,程福明,刘毅,孙康宁.不同分散剂制备的石墨烯纳米片/双相磷酸钙生物复合材料及其力学性能研究[J].人工晶体学报,2013(05):927-932. |
| [11] | 刘春梅,肖贤波,刘念华.吸附缺陷对armchair型石墨烯纳米条带输运性质的影响[J].人工晶体学报,2011(01):104-108. |
| [12] | 孙建平,缪应蒙,曹相春.基于密度泛函理论研究掺杂Pd石墨烯吸附O2及CO[J].物理学报,2013(03):262-269. |
| [13] | 刘其军,刘正堂,冯丽萍.A-La2O3电子结构和光学性质的第一性原理计算[J].计算物理,2010(05):752-758. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%