用热重法研究稀土元素Y和Ce对定向凝固镍基高温合金 DZ444高温氧化行为的影响，用X 射线衍射仪和扫描电镜等观察和分析氧化膜组成和形貌。结果表明：合金在700、850和950℃下的恒温氧化动力学均符合抛物线规律，稀土元素的添加对其无影响；然而，添加稀土元素使其氧化激活能由257.6 kJ/mol 降低至246.8 kJ/mol；DZ444合金氧化膜分为3层：外层为疏松的 Cr2O3、TiO2和(Cr0.88Ti0.12)2O3的混合物；中间层为Cr2O3；内氧化物层为 Al2O3。稀土元素未改变合金氧化膜的组成。稀土元素极易偏聚在合金表面，促进保护性 Cr2O3膜的形成，从而阻止合金的进一步氧化，并能有效抑制合金的内氧化。
The effect of rare earth elements Y and Ce on the oxidation behavior of Ni-based superalloy DZ444 at elevated temperatures was studied by TGA method. The composition and morphology of the oxide films of DZ444 alloy were measured by XRD and SEM. The results indicate that rare earth elements has no effect on the oxidation kinetics, which obey parabolic law at 700, 850 and 950 ℃. However, the values of activation energy decrease from 257.6 kJ/mol to 246.8 kJ/mol when Y and Ce elements are added to the alloy. The oxide films of DZ444 alloy consist of three layers, loose upper layer consists of TiO2, Cr2O3 and (Cr0.88Ti0.12)2O3, compact intermediate layer is mainly Cr2O3, and discrete internal oxides are Al2O3. The composition of oxide films is not changed by rare earth elements, which can easily segregate on the surface of the alloy and accelerate the formation of protective oxidation film to prevent further oxidation. Therefore, it can be concluded that the addition of rare earth elements Y and Ce can effectively inhibit the development of internal oxidation.
参考文献
| [1] | BERTHOD P .Kinetics of high temperature oxidation and chromia volatilization for a binary Ni-Cr alloy[J].Oxidation of Metals,2005,64(3/4):235-252. |
| [2] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001:5-150. |
| [3] | 郭建亭.高温合金材料学[M].北京:科学出版社,2008:317-319. |
| [4] | SIMS C T;HAGEL W C.In superalloys II[M].New York:John Wiley & Sons,1987:187-189. |
| [5] | LY. Sheng;F. Yang;T.F. Xi;C. Lai;H.Q, Ye .Influence of heat treatment on interface of Cu/Al bimetal composite fabricated by cold rolling[J].Composites, Part B. Engineering,2011(6):1468-1473. |
| [6] | Liyuan Sheng;Lijun Wang;Tingfei Xi;Yufeng Zheng;Hengqiang Ye .Microstructure, precipitates and compressive properties of various holmium doped NiAl/Cr(Mo, Hf) eutectic alloys[J].Materials & design,2011(10):4810-4817. |
| [7] | 郭建亭,袁超,侯介山.稀土元素在NiAl合金中的作用[J].金属学报,2008(05):513-520. |
| [8] | BERANGER G;ARMANET F;LAMBERTIN M.Active elements in oxidation and their properties[A].Berlin:Elsevier Applied Science,1989:33-51. |
| [9] | 梁艳,龙媛媛,付广艳.稀土元素对合金抗高温氧化和耐腐蚀性能的影响[J].四川化工,2004(03):37-38,41. |
| [10] | 李云,袁超,郭建亭,杨洪才.铸造镍基高温合金K35的氧化动力学[J].东北大学学报(自然科学版),2003(01):75-78. |
| [11] | 李云,尚海波,郭建亭,袁超,杨洪才.铸造镍基高温合金K35的高温氧化行为[J].金属学报,2003(07):749-754. |
| [12] | 陈武 .高温高发射率红外辐射涂层的制备与研究[D].武汉理工大学,2008. |
| [13] | 王民庆,曲敬龙,殷铁志,盛俊英,邓群,吕旭东.GH4720Li合金高温氧化行为研究[J].钢铁研究学报,2010(09):28-33. |
| [14] | HUSSAIN N;SHAHID K A;KHAN I H;RAHAMAN S .Oxidation of high-temperature alloys(superalloys)at elevated temperatures in air:II[J].Oxidation of Metals,1995,43(3/4):363-378. |
| [15] | 梁婷 .Ni-Cr-Al合金高温氧化及影响机理研究[D].沈阳师范大学,2011. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%