采用溶胶-凝胶法制备氧化锌纳米材料并考察了其抗菌性能.研究发现,通过调控醋酸锌-无水乙醇-氢氧化钠反应体系的反应温度、反应时间、反应物浓度以及反应体系中的水含量可以控制纳米ZnO的粒径分布;以金黄色葡萄球菌和大肠杆菌作为革兰氏阳性菌和革兰氏阴性菌的代表,用抑菌圈法考察了材料的抗菌性能,结果表明,溶胶-凝胶法合成的ZnO纳米材料抑菌效果明显优于相应的水热法产物和市售产品,且与其粒径分布密切相关;在实验条件下,ZnO材料对大肠杆菌和金黄色葡萄球菌的抑制性能随ZnO纳米材料的粒径增大在5nm左右出现一个极值,材料的粒径小于或大于5nm,其抗菌效果均变差.
参考文献
| [1] | Liuh L;Yang T C K .[J].Process Biochemistry,2003,39:475-481. |
| [2] | Sawai J. .Quantitative evaluation of antibacterial activities of metallic oxide powders (ZnO, MgO and CaO) by conductimetric assay[J].Journal of Microbiological Methods,2003(2):177-182. |
| [3] | Zhou Z W;Liu J J;Chu L S .[J].Materials Science Forum,2005,486-487:77-80. |
| [4] | Yamamoto O .[J].International J Inorg Mater,2001,3:643-646. |
| [5] | 俞建群,贾殿赠,郑毓峰,忻新泉.纳米氧化镍、氧化锌的合成新方法[J].无机化学学报,1999(01):95-98. |
| [6] | Vayssieres L .[J].Advanced Materials,2003,15:464-466. |
| [7] | Kong X Y;Ding Y;Yang R et al.[J].Science,2004,303:1348-1351. |
| [8] | Spanhel L;Anderson M A .[J].Journal of the American Chemical Society,1991,113:2826-2833. |
| [9] | Menlenkamp E A .[J].Journal of Physical Chemistry B,1998,102:5566-5572. |
| [10] | Tokumoto M S;Pulcinelli S H;Santilli C V et al.[J].Journal of Physical Chemistry B,2003,107:568-574. |
| [11] | Tokumoto M S;Briois V;Santilli C V .[J].Journal of Sol-Gel Science and Technology,2003,26:547-551. |
| [12] | Bonanni M.;Lerch M.;Fuglein E.;Muller G.;Jermann F.;Spanhel L. .Conversion of colloidal ZnO-WO3 heteroaggregates into strongly blue luminescing ZnWO4 xerogels and films[J].Chemistry of Materials,1998(1):304-310. |
| [13] | 周群英;高廷耀.环境工程微生物学[M].北京:高等教育出版社,2000 |
| [14] | 隆泉,郑保忠,周应揆,柳清菊.新型纳米无机抗菌剂的抗菌性能研究1.对金黄色葡萄球菌和白色念珠菌的抗菌作用[J].功能材料,2006(02):274-276. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%