以AR中间相沥青为原料,采用中间相沥青自发泡法在初始发泡压力为3MPa、发泡温度在390～450℃范围内制备了4种炭泡沫.利用SEM观察了炭泡沫的孔隙结构,并测定了其体积密度、抗压强度和导热系数,考察了发泡温度对炭泡沫结构及性能的影响.结果表明,采用较低的发泡温度(＜430℃)可以消除大的孔隙缺陷;当发泡温度为410℃时,炭泡沫导热系数最高,为0.256W/(m·K).
参考文献
| [1] | Ford W .Method of Making Cellular Refractory Thermal Insulating Material[P].USP:3121050,1964. |
| [2] | Klett J.;Romine E.;Walls C.;Burchell T.;Hardy R. .High-thermal-conductivity, mesophase-pitch-derived carbon foams: effect of precursor on structure and properties[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(7):953-973. |
| [3] | Klett J W;Mcmillan A D;Gallego N C et al.[J].Carbon,2004,42(8-9):1849-1852. |
| [4] | Klett J W .Process for making Carbon Foam[P].USP:6033506,2000. |
| [5] | Nidia C. Gallego;James W. Klett .Carbon foams for thermal management[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(7):1461-1466. |
| [6] | 李凯,栾志强.中间相沥青基炭泡沫[J].新型炭材料,2004(01):77-78. |
| [7] | 曹敏,张书,周建民,王永刚.炭素泡沫材料的制备和应用[J].材料科学与工程学报,2004(04):613-616. |
| [8] | 沈曾民,戈敏,迟伟东,刘辉.中间相沥青基炭泡沫体的制备、结构及性能[J].新型炭材料,2006(03):193-201. |
| [9] | 李同起,王成扬.中间相沥青基泡沫炭的制备与结构表征[J].无机材料学报,2005(06):1438-1444. |
| [10] | Marsh H;Martinez-Escandell M;Rodriguez-Reinoso F .[J].Carbon,1997,37(03):363-390. |
| [11] | 邱海鹏,郭全贵,宋永忠,翟更太,宋进仁,刘朗.石墨材料导热性能与微晶参数关系的研究[J].新型炭材料,2002(01):36-40. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%