以异佛尔酮二异氰酸酯(IPDI)、聚碳酸酯二醇(PCDL)、3,3',4,4'-二苯甲酮二酐(BTDA)和聚醚胺(ATA)为原料,采用A2+B3法合成了具有高度支化结构的聚氨酯-酰亚胺(HBPUI).通过红外光谱(FT-IR)对结构进行了表征.采用旋转黏度计、差式扫描量热分析(DSC)、热重分析(TGA)、电子拉力机对产物的性能进行了测试.结果表明,与线性聚氨酯-酰亚胺(LPUI)相比,HBPUI具有较低的黏度和较高的Tg;HBPUI的热分解温度达到300℃以上,与高度支化聚氨酯相比,热稳定性得到明显提高;力学测试表明,HBPUI的拉伸强度随硬段含量和[A2]/[B3]的增大而增大,而断裂伸长率呈下降趋势.
参考文献
| [1] | Yeganeh H.;Khodabadi FN.;Barikani M. .Synthesis and properties of novel thermoplastic poly(urethane-imide)s[J].European Polymer Journal,2000(10):2207-2211. |
| [2] | Deligoz H;Yalcinyuva T;Ozgumus S .A novel type of Si-containing poly(urethane-imide)s: synthesis, characterization and electrical properties[J].European Polymer Journal,2005(4):771-781. |
| [3] | 曾少敏,姚畅,陈爱芳,易昌凤,徐祖顺.超支化聚氨酯的合成及应用[J].高分子通报,2008(03):52-57. |
| [4] | Fornof AR;Glass TE;Long TE .Degree of branching of highly branched polyurethanes synthesized via the oligomeric A(2) plus B-3 methodology[J].Macromolecular chemistry and physics,2006(14):1197-1206. |
| [5] | Mishra AK;Chattopadhyay DK;Sreedhar B;Raju KVSN .FT-IR and XPS studies of polyurethane-urea-imide coatings[J].Progress in Organic Coatings: An International Review Journal,2006(3):231-243. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%