The kinetic curve of the high-temperature oxidation of austenitie stainless steel Crl8Ni11 Cu3Al3MnNb at different temperatures was measured by weighting method. It is showed that the oxidation curves at 700 and 800 ℃ followed the parabolic law, and the steel presented an excellent anti-oxidation. The surface morphology and structure of the oxide film were studied by scanning electron microscopy and X-ray diffraction methods. A dense oxide film was attained at 700 and 800 ℃, mainly composed of the hexagonal Al2 O3, Fe2 O3, and a small amount oxide of Cr at 700 ℃. At 900 ℃ the oxide film started to delaminate, and was composed of （Cr,Fe）2O3 and the spinel CuCrMnO4 and Fe（Cr, Al） 2O3.
参考文献
| [1] | Sourmail T. .Precipitation in creep resistant austenitic stainless steels [Review][J].Materials Science and Technology: MST: A publication of the Institute of Metals,2001(1):1-14. |
| [2] | Taneike M;Abe F;Sawada K .Creep-Strengthening of Steel at High Temperatures Using Nano-Sized Carbonitride Dispersions[J].Nature,2003,424(6946):294. |
| [3] | Opila E J .Volatility of Common Protective Oxides in High- Temperature Water Vapor:Current Understanding and Unan-swered Questions[J].Materials Science Forum,2004,461-464:765. |
| [4] | Pintb A;Peraldi R;Maziasz P Z .The Use of Model Alloys to Develop Corrosion Resistant Stainless Steels[J].Materials Science Forum,2004,461-464:815. |
| [5] | BRADY M P,YAMAMOTO Y,LU Z P,MAZIASZ P J,LIU C T,PINT B A,SANTELLA M L.一种在表面形成Al2O3膜的新型耐热奥氏体不锈钢[J].自然杂志,2008(04):189-193,插1. |
| [6] | Brady M P;Yamamoto Y;Santella M L et al.Effect of Minor Alloy Additions and Oxidation Temperature on Protective Alumina Scale Formation in Creep-Resistant Austenitic Stainless Steels[J].Scripta Materialia,2007,57:1117. |
| [7] | Yamamoto Y;Brady M P;Lu Z P et al.Alumina-Forming Austenitie Stainless Steels Strengthened by Laves Phase and MC Carbide Precipitates[J].Metallugical and Materials Transactions,2007,38A:2737. |
| [8] | Yamamoto Y;Brady MP;Lu ZP;Maziasz PJ;Liu CT;Pint BA;More KL;Meyer HM;Payzant EA .Creep-resistant, Al2O3-forming austenitic stainless steels.[J].Science,2007(5823):433-436. |
| [9] | Satyanarayana D V V;Malakondaiah G;Sarma D S .Steady State Creep Behaviour o{ NiA1 Hardened Austenitic Steel[J].Materials Science and Engineering,2002,323A:119. |
| [10] | Yoshiatsu Sawaragi;Kazuhiro Ogawa;Shinichiro Kato.Development of the Economical 18-8 Stainless Steel(Super304H)Having High Elevated Temperature Strength for Fossil Fired Boillers[A].Osaka and Tokyo:Sumitomo Metal Industries Ltd,1992:50. |
| [11] | Sundararajan T;Kuroda S;Kawakita J;Seal S .High temperature corrosion of nanoceria coated 9Cr-1Mo ferritic steel in air and steam[J].Surface & Coatings Technology,2006(6):2124-2130. |
| [12] | 唐庆新,刘靖,韩静涛.奥氏体耐热不锈钢309S高温抗氧化性能研究[J].钢铁研究学报,2009(10):43-47. |
| [13] | 杨照明,韩静涛,刘靖,刘彪.奥氏体耐热不锈钢310S的抗高温氧化性能研究[J].热加工工艺,2006(14):33-34,57. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%