分别将30%、40%、50%混合材与水泥熟料复合,制备高强度复合水泥.混合材主要为矿渣、活化粉煤灰和活化煤矸石.通过砂浆强度测试及孔结构测试等技术,对复合水泥的力学性能、水化过程和水化机理进行了分析研究.试验结果表明,当3种混合材复掺时,制备的复合水泥的强度较高.复合水泥28d抗压强度最高达到65MPa,各试样的抗压强度均超过50MPa,且后期强度继续增大.从孔结构结果可看出,制备的复合水泥的水泥石有较多的凝胶孔和较低的总孔隙率.
参考文献
| [1] | Bagel L .Strength and pore structure of ternary blended cement mortars containing blast furnace slag and silica fume[J].Cement and Concrete Research,1998,28:1011. |
| [2] | Li D;Wu X;Shan J et al.The influence of compound admixtures on the properties of high-content slag cement[J].Cement and Concrete Research,2000,30:45. |
| [3] | 徐彬;蒲心诚 .矿渣玻璃体分相结构与矿渣潜在水硬活性本质的关系探讨[J].硅酸盐学报,1997,25(06):729. |
| [4] | Li D;Xu Z;Luo Z et al.The activation and hvdration of glassy cementitious materials[J].Cement and Concrete Research,2002,32:1145. |
| [5] | Fraay A L A;Bijen J M;Dehaan Y M .The reaction of fly ash in concrete,a critical examination[J].Cement and Concrete Research,1989,19:235. |
| [6] | 宋旭艳,宫晨琛,李东旭.煤矸石活化过程中结构特性和力学性能的研究[J].硅酸盐学报,2004(03):358-363. |
| [7] | 宫晨琛,李东旭,王晓钧.增钙煅烧煤矸石的活性评价及其作用机理[J].硅酸盐学报,2005(07):842-845,852. |
| [8] | 廉慧珍;童良;陈恩义.建筑材料物相研究基础[M].北京:清华大学出版社,1996:105. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%