Understanding the behavior of weldment at elevated temperatures and especially the corrosion behavior has become an object of scientific investigation recently. Investigation has been carried out on friction welded AISI 4140 and AISI 304 in molten salt of K2SO4-60% NaCI environment at 550, 600 and 650 ℃ under cyclic condition. The resulted oxide scales in the weldment have been characterized systematically by surface analytical techniques. From the results of the experiments~ it is observed that the scale thickness on low alloy steel side was higher than that on stainless steel side. Furthermore, weld interface has been found to be more susceptible to degradation than base metals due to inter diffusion of element across the interface and the formation of intermetallic compound. The influences of welding parameters and the temperature of exposure on the hot corrosion behavior of the weldment were discussed in this paper.
参考文献
| [1] | N. Arivazhagan;S. Singh;S. Prakash .High temperature corrosion studies on friction-welded dissimilar metals[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2006(1/2):222-227. |
| [2] | R. Paventhan;P.R. Lakshminarayanan;V. Balasubramanian .Fatigue behaviour of friction welded medium carbon steel and austenitic stainless steel dissimilar joints[J].Materials & design,2011(4):1888-1894. |
| [3] | L.W. Tsay;Y.C. Liu;M.C. Young .Fatigue crack growth of AISI 304 stainless steel welds in air and hydrogen[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):204-210. |
| [4] | N. Arivazhagan;Surendra Singh;Satya Prakash;G.M. Reddy .Investigation on AISI 304 austenitic stainless steel to AISI 4140 low alloy steel dissimilar joints by gas tungsten arc, electron beam and friction welding[J].Materials & design,2011(5):3036-3050. |
| [5] | N. Ozdemir;F. Sarsilmaz;A. Bascalik .Effect of rotational speed on the interface properties of friction-welded AISI 304L to 4340 steel[J].Materials & Design,2007(1):301-307. |
| [6] | D.G. Hattingh;D.LH. Bulbring;A. Els-Botes;M.N. James .Process parameter influence on performance of friction taper stud welds in AISI 4140 steel[J].Materials & design,2011(6):3421-3430. |
| [7] | N. Venkateswara Rao;G. Madhusudhan Reddy;S. Nagarjuna .Weld overlay cladding of high strength low alloy steel with austenitic stainless steel - Structure and properties[J].Materials & design,2011(4):2496-2506. |
| [8] | R. K. Singh Raman;B. C. Muddle .High temperature oxidation in the context of life assessment and microstructural degradation of weldments of 2.25Cr-1Mo steel[J].International Journal of Pressure Vessels and Piping,2002(8/10):585-590. |
| [9] | V.V. Satyanarayana;G. Madhusudhan Reddy;T. Mohandas .Dissimilar metal friction welding of austenitic-ferritic stainless steels[J].Journal of Materials Processing Technology,2005(2):128-137. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%