研究了SBS在不同频率、不同振幅及紫外作用下的动态疲劳行为.应用红外和扫描电镜(SEM)研究了试样表面结构和形貌的变化.结果表明,随着频率和应变的增大,疲劳寿命逐渐降低,紫外能加速材料的断裂失效;单纯改变物理因素对试样表面影响不大,而紫外照射后红外谱图中峰强明显发生变化;SEM结果显示试样表面在疲劳后出现不同程度的裂纹,而施加了紫外辐照的试样表面裂纹则变得明显,破坏严重.
参考文献
[1] | Kim GH;Lu H .Characteristics of accelerated lifetime behavior of polycarbonate under athermal and high loading frequency conditions[J].Polymer Testing,2007(7):839-845. |
[2] | Gang Tao;Zihui Xia .Mean stress/strain effect on fatigue behavior of an epoxy resin[J].International Journal of Fatigue,2007(12):2180-2190. |
[3] | Kaang S;Jin YW;Huh Y;Lee WJ;Im WB .A test method to measure fatigue crack growth rate of rubbery materials[J].Polymer Testing,2006(3):347-352. |
[4] | Sousa AR;Amorim KLE;Medeiros ES;Melo TJA;Rabello MS .The combined effect of photodegradation and stress cracking in polystyrene[J].Polymer Degradation and Stability,2006(7):1504-1512. |
[5] | Rui Chen;David R.Tyler .Origin of Tensile Stress-Induced Rate Increases in the Photochemical Degradation of Polymers[J].Macromolecules,2004(14):5430-5436. |