研究了AZ91D镁合金在应变诱发熔化激活法处理过程中形变率和形变温度对组织的影响.结果表明: 形变温度为280℃时, 随着形变率增加, 部分枝晶臂逐渐伸长, 枝晶破断现象加剧; 形变率为20%时, 随着形变温度的提高, 组织的形变方式逐渐由以枝晶断裂为主转变为带有方向性的弯曲.AZ91D合金在580℃等温10min所获得的半固态组织, 随着形变率增加, 球状晶粒尺寸减小, 圆整度提高; 随形变温度的提高, 固相颗粒的偏聚现象减轻.
参考文献
| [1] | Jae Chan Choi;Hyung Jin Park .Microstructural characteristics of aluminum 2024 by cold working in the SIMA process[J].Journal of Materials Processing Technology,1998(1/3):107-116. |
| [2] | Flemings M C .Behavior of metal alloys in the semisolid state[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22:957-980. |
| [3] | Charles V .Elaboration of semisolid alloys by means of new electron-magnetic rheocasting process[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1992,23:189-205. |
| [4] | 陈体军,郝远.金属的半固态成形技术与应用[J].铸造,2001(11):645-649. |
| [5] | 陈体军,郝远.金属的半固态成形技术与应用[J].铸造,2001(11):645-649. |
| [6] | 左宏志,刘昌明,邹茂华,谷忠明,范增,李德全,吴均.ZL112Y压铸铝合金摩托车零件的半固态高压铸造成形[J].中国有色金属学报,2003(04):949-955. |
| [7] | 左宏志,刘昌明,邹茂华,谷忠明,范增,李德全,吴均.ZL112Y压铸铝合金摩托车零件的半固态高压铸造成形[J].中国有色金属学报,2003(04):949-955. |
| [8] | 杨红亮,张质良,I.Ohnaka,H.Yasuda,A.Sugiyama,T.Ohmichi.ZL101合金半固态二次加热[J].中国有色金属学报,2003(03):626-630. |
| [9] | 杨红亮,张质良,I.Ohnaka,H.Yasuda,A.Sugiyama,T.Ohmichi.ZL101合金半固态二次加热[J].中国有色金属学报,2003(03):626-630. |
| [10] | 杨红亮;张质良.半固态金属制备技术[J].中国有色金属学报,2002(Z2):126-131. |
| [11] | YANG Hong liang;ZHANG Zhi liang.Production technique of semi-solid slurries[J].The Chinese Journal of Nonferrous Metals,2002(Z2):126-131. |
| [12] | 田文彤,罗守靖,张广安.半固态LC4合金的屈服应力[J].中国有色金属学报,2002(01):82-86. |
| [13] | 田文彤,罗守靖,张广安.半固态LC4合金的屈服应力[J].中国有色金属学报,2002(01):82-86. |
| [14] | 王开,刘昌明,邹茂华,韩兆堂.ZL112Y铝合金半固态压铸过程微观组织的演变[J].中国有色金属学报,2003(04):956-962. |
| [15] | 王开,刘昌明,邹茂华,韩兆堂.ZL112Y铝合金半固态压铸过程微观组织的演变[J].中国有色金属学报,2003(04):956-962. |
| [16] | 朱鸣芳;苏华钦.预形变量和半固态等温温度对触变组织的影响[J].铸造,1996(01):8-10. |
| [17] | ZHU Ming-fang;SU Hua-qin.The effect of the previous deformation and the isothermal temperature in semi--solid state on the thixotropic microstructure[J].Foundry,1996(01):8-10. |
| [18] | Kojima Y;Aizawa T;Kamado S.Magnesium Alloys 2000[M].Switzerland:Trans Tech Publications Ltd,2000 |
| [19] | Decker R F .The renaissance in magnesium[J].Current Advances in Materials and Processes,1998,154(09):31-35. |
| [20] | 余琨,黎文献,王日初,马正青.变形镁合金的研究、开发及应用[J].中国有色金属学报,2003(02):277-288. |
| [21] | 余琨,黎文献,王日初,马正青.变形镁合金的研究、开发及应用[J].中国有色金属学报,2003(02):277-288. |
| [22] | 陈体军,郝远,陆松,许广济.ZA27合金在SIMA处理过程中形变量和等温温度对组织的影响[J].金属热处理学报,2000(01):26-31. |
| [23] | 陈体军,郝远,陆松,许广济.ZA27合金在SIMA处理过程中形变量和等温温度对组织的影响[J].金属热处理学报,2000(01):26-31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%