通过正交试验筛选确定了Al-Zr-In-Si牺牲阳极材料的最佳配比为Zn5．5％，In0．020％，Si0．11％，Fe0．12％。并对其电化学性能进行研究。结果表明，Al-5．5Zn-0．02In-0．11Si牺牲阳极材料的电化学性能指标包括开路电位、工作电位、实际电化学容量、电流效率、表面溶解形貌等，均达到或超过国家标准。
The electrochemical performance of 9 types of Al-Zn-In-Si sacrificial anode materials with different amounts of Zn, In, Si and Fe were studied in natural seawater. The test results showed that the electrochemical performance of Al-Zn-In-Si meets and exceeds the national standard. The composition of Al-Zn-In-Si anode was optimized through orthogonal test. The optimum contents of alloy elements were as follows.. Zn 5.5 % In 0. 020% Si 0. 11%; Fe 0. 12%.
参考文献
| [1] | 李异.铝合金牺牲阳极在南海海泥中的性能研究[J].腐蚀科学与防护技术,1991(01):22. |
| [2] | 李异,李永广.铝牺牲阳极在热海泥中的电化学性能[J].材料开发与应用,2001(03):19-22. |
| [3] | 李威力,闫永贵,陈光,马力.Al-Zn-In系牺牲阳极低温电化学性能研究[J].腐蚀科学与防护技术,2009(02):122-124. |
| [4] | 廖海星,朱鸿赫,齐公台.温度对铝合金牺牲阳极活化溶解行为的影响[J].华中科技大学学报(自然科学版),2004(02):114-116. |
| [5] | 马丽杰,宋曰海,郭忠诚,樊爱民.Al-Zn-In-Cd牺牲阳极材料的电化学性能研究[J].材料开发与应用,2004(01):32-34. |
| [6] | 赵月红,林乐耘,刘增才,徐杰.铝合金牺牲阳极微观组织的不均匀性对其腐蚀的影响[J].稀有金属,2000(05):341-344. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%