以酚醛树脂为炭前驱体,KOH作活化剂,通过调节炭化温度在相同活化条件下制备了具有不同孔隙结构的活性炭材料.N_2吸附测试表明随着炭化温度降低,活性炭材料比表面积先增大后减小,孔容则不断增大.其中,550℃炭化样品与KOH反应活性最佳,可制得比表面积为2983m~2/g,总孔容为1.58cm~3/g,中孔孔容达到0.59cm~3/g的活性炭材料.采用直流充放电法、交流阻抗法和循环伏安法测定以上述多孔炭为电极材料的双电层电容器的电化学性能,结果表明,PF550活性炭材料电容性能最佳,在有机电解液中100mA/g充放电时,比电容达到160F/g,电流密度增大50倍容量保持率达到82%,显示出良好的功率特性;活性炭材料中存在一定比例的中孔不仅可以改善电极材料的功率特性,而且可以提高微孔的利用率.

Activated carbon with distinct pore structure used for electric double layer capacitor ( EDLC) was prepared with resol phenolic resin as raw material and KOH as activator by chemical activation.The specific surface area and pore structure of activated carbon were characterized by nitrogen adsorption isotherm at 77K.The pore volume and mesoporosity of activated carbons increased with decrease of carbonization temperature,while the BET surface area increased firstly and decreased afterwards.The electrochemical behaviors were characterized by means of galvanostatic charging/discharging,cycle voltammetry and impedance spectroscopy.The correlation between electrochemical properties and pore structure was investigated.The results show that PF550 exhibited excellent specific dc capacitance over 160F/g at 100mA/g and the capacitance maintenance achieve 82% at 5000mA/g in organic electrolyte.The high current charge/discharge performance was improved by a reasonable mesoporosity and somewhat wide pore size distribution.

参考文献

[1] Andrew B .[J].Journal of Power Sources,2000,91(01):37-50.
[2] Teng H;Chang Y J;Hsieh C T .[J].Carbon,2001,39:1981-1987.
[3] Lee J;Yoon S;Hyeon T.[J].Chemical Communications,1999(21):2177-2178.
[4] Endo M.;Kim YJ.;Ohta H.;Ishii K.;Inoue T.;Hayashi T.;Nishimura Y. Maeda T.;Dresselhaus MS. .Morphology and organic EDLC applications of chemically activated AR-resin-based carbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(14):2613-2626.
[5] Xing Wei;Zhuo Shuping;Gao Xiuli .[J].Materials Letters,2009,63:1311-1313.
[6] Juárez-Galán J M;Silvestre-Albero A;Silvestre-Albero J et al.[J].Microporous and Mesoporous Materials,2009,117:519-521.
[7] 陈鸯飞,陈智琴,刘洪波.酚醛树脂中亚甲基对热降解的影响[J].高分子学报,2008(05):399-404.
[8] Miguel G S;Fowler G D;Sollars C J .[J].CARBON,2003,41:1009-1016.
[9] Moreira R F P M;Jose'H J;Rodrigues A E .[J].Carbon,2001,39:2269-2275.
[10] Ruthven D M.Principles of Adsorption and Desorption Processes[M].New York:wiley,1984:55-58.
[11] Chmiola J;Yushin G;Gogotsi Y;Portet C;Simon P;Taberna PL .Anomalous increase in carbon capacitance at pore sizes less than 1 nanometer[J].Science,2006(5794):1760-1763.
[12] Raymundo-Pinero E;Kierzek K;Machnikowski J et al.[J].Carbon,2006,44:2498-2507.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%