采用低剪切应力分散混合法制备了PP/CaCO3纳米复合材料(标记为C-1,C-2),研究了纳米粒子分散状态对PP结晶的影响.扫描电镜(SEM)显示CaCO3以纳米尺度均匀分散在C-1中,而在C-2中则局部团聚.示差扫描量热分析(DSC)表明,C-1熔融峰温和结晶度相对纯PP分别提高了4.1 ℃和6.0%;而C-2的熔融峰温降低4.6 ℃,结晶度降低9.1%.广角X射线衍射(WAXD)显示C-1和C-2晶型没有变化,C-1晶面衍射强度和微晶尺寸较纯PP明显增大;而C-2衍射峰与纯PP相似,微晶尺寸减小.
参考文献
| [1] | Roy R;Kormarneni S .[J].Materials Research Society Symposium Proceedings,1984,32:347-350. |
| [2] | Avella M;Cosco S;Di Lorenzo ML;Di Pace E;Errico ME .Influence of CaCO3 nanoparticles shape on thermal and crystallization behavior of isotactic polypropylene based nanocomposites[J].Journal of thermal analysis and calorimetry,2005(1):131-136. |
| [3] | Saujanya C.;Radhakrishnan S. .Structure development and crystallization behaviour of PP/nanoparticulate composite[J].Polymer: The International Journal for the Science and Technology of Polymers,2001(16):6723-6731. |
| [4] | 刘正英,于润泽,杨鸣波,冯建民,杨伟,尹波.聚合物/纳米碳酸钙复合材料的制备[J].高分子学报,2007(01):53-58. |
| [5] | 史大刚,姚子华,仇满德,谷志杰,延永柱,马晓莉.聚丙烯/纳米粒子复合材料结晶行为的研究[J].现代塑料加工应用,2005(01):19-21. |
| [6] | Avella M;Errico M E;Martelli S et al.[J].Applied Organometallic Chemistry,2001,15:435-439. |
| [7] | 杨军,刘万军,陈广新,刘景江.超细CaCO3的粒子尺寸对PP结晶行为的影响[J].高分子学报,2001(03):383-386. |
| [8] | Li J X;Cheung W L .[J].Polymer,1999,40:2085-2088. |
| [9] | 莫志深;张宏放.晶态聚合物结构和X射线衍射[M].北京:科学出版社,2003:44. |
| [10] | Bas C;Grilie F .[J].European Polymer Journal,1995,31(10):911-921. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%