扫描间距对激光相变硬化组织及其性能的影响

腐蚀科学与防护技术, 2010, 22(1): 24-27.

扫描间距对激光相变硬化组织及其性能的影响

李刚 , 邱星武 , 任鑫 , 邱玲

阜新 123000

朝阳 122504

1.1School of Materials Science and Engineering

Liaoning Technical University

Fuxin 123000

Dynamic

Lingyuan Iron &

Steel Group CO.

关键词：激光相变硬化 , 40Cr steel , scanning space , microstructure , property

Influence of Scanning Space on Microstructure and Propertics of Laser Transformation Hardening

LI Gang , QIU Xing-wu , REN Xin , QIU Ling

Keywords： laser transformation hardening , 40Cr钢 , 扫描间距 , 组织 , 性能

利用HL-1500横流CO₂激光加工机对40Cr钢表面进行激光相变硬化处理,利用扫描电镜、X射线衍射仪、显微硬度计、恒电位仪、磨损试验机等研究了不同扫描间距对激光相变硬化层组织性能的影响.结果表明：激光相变硬化层主要由Fe、Fe₃C、Fe-Cr、Cr₃C₂等相组成.当扫描间距为8 mm时,回火作用显著,扫描间距为16 mm时,回火作用不明显.试样的显微硬度随扫描间距的增大先升高后降低,扫描间距为12 mm时,试样的平均显微硬度最高,为794.7 MPa.随着扫描间距的增加,耐蚀性和耐磨性均增强.

Laser surface hardening was carried out by HL-1500 CO₂ laser machine on 40Cr steel,and the influence of scanning space on microstructure and properties of laser transformation hardened layers were investigated by means of scanning electron microscope,X-ray diffractometer,microhardness meter,potentiostat and abrasive wear testing machine etc.The result indicated that,the laser transformation hardened layer is mainly consisted of Fe、Fe₃C、Fe-Cr and Cr₃C₂.The tempering effect is obvious when scanning space is 8 mm,and when scanning space is 16 mm,the tempering effect is not obvious.The microhardness of the samples increased at first and then decreased with the increasing of the scanning space.The maximum microhardness 794.7 MPa is obtained when scanning space is 12 mm.Both the corrosion resistance and wear resistance are enhanced with the increasing of the scanning space.

参考文献

[1]

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
李刚邱星武任鑫邱玲
在百度学术搜索
李刚邱星武任鑫邱玲
在万方数据库搜索
李刚邱星武任鑫邱玲
在CNKI搜索
李刚邱星武任鑫邱玲

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网