CaO-MgO-P2O5-SiO2系微晶玻璃是一种新型医学生物材料,该材料不仅具有良好的生物相容性,还具有一定的力学性能．本文采用差热分析(DTA)方法对以TiO2作为晶核剂的该系生物微晶玻璃的析晶动力学参数进行了测定。所得数据经计算机拟合后,其结果表明:在一定范围内引入TiO2(≤８．７wt%)能降低该系玻璃的析晶活化能Ｅ,有促进玻璃析晶的作用;当TiO2含量达到８．７wt%时,Ｅ达到最小值;当TiO2含量＞8.7wt%时,Ｅ值反而回升．晶化指数ｎ与该玻璃体系中加入TiO2的变化规律与Ｅ值随TiO2的变化规律是一致的．
CaO-MgO-P2O5-SiO2 glass-ceramic is a new medicinal biologic material. It not only has good
biocompatibility but also improves mechanical properties. The kinetic parameters of this glass-ceramic were calculated by differential thermal
analysis (DTA) and the JMA equation. The results indicate that the content of TiO2 effects on the crystallization activation energy (E) and the
crystal growth index (n). E increases with the increasing of TiO2 content. And E reaches a max value when TiO2 content is about
8.7%. When TiO2 content increases further (>8.7%), E decreases inversely. The rule of n vs TiO2 content is consistent with that
of E vs TiO2 content.
参考文献
| [1] | Kokubo T, Shigematsu M, et al. Bull. Inst. Chem. Res. Kyoto Univ., 1982, 60: 260--268. [2] Nakamura T, Yamamuro T, Higashi S, et al. J. Biomed. Mater. Res., 1985, 19: 686--698. [3] Kasuga T, Nakagawa K, et al. J. Mater. Sci., 1987, 22: 3721--3724. [4] Stookey W D. British Patent, No.829449. [5] Potherty P E, Lee D W, Davis R S. J. Amer. Ceram. Soc., 1967, 50: 77--81. [6] Barry T I, Clinton D, Lay L A, et al. J. Mater. Sci., 1970, 5 (2): 117--121. [7] Zdaniewski W. J. Amer. Ceram. Soc., 1975, 58 (5-6): 163--169. [8] Duan R G, Liang K M, Gu S R. J. Eur. Ceram. Soc., 1998, 18: 1729--1735. [9] 段仁官, 梁开明, 顾守仁. 玻璃与搪瓷, 25 (3): 1--4. [10] 陈镜泓, 李传儒. 热分析及其应用, 北京: 科学出版社, 1985. 266. [11] Matecki M, Lucas J. J. Non-Cryst. Solids, 1993, 162: 51. [12] Johnson W A, Mehl R F. Trans AIME, 1939, 135: 416--458. [13] Avrami M. J. Chem. Phys., 1939, 7: 1103--1112. [14] Piloyan G O, Ryabchikov I D, Novikova O S. Nature (London), 1966, 212: 1229--1229. |