SrAl2 O4: Eu2+ , Dy3+ long afterglow phosphors were prepared by chemical coprecipitation method. Ammonium carbonate and ammonium hydrogen carbonate were used as the precipitants. The preparation of the SrAl2 O4: Eu2+ ,Dy3 + precursor was completed at room temperature by controlling the concentration of the metal-salt solution, pH value of the system, etc. The phosphors were prepared by sintering the precursor at 1000 ～ 1200 ℃ in a weak reducing atmosphere for 2 h. The XRD, SEM, excitation spectra, emission spectra and afterglow decay of the samples were tested and the optimal synthesis conditions of the SrAl2O4: Eu2+ , Dy3+ long afterglow phosphors prepared by precipitation method were determined. The phosphor which had good luminescent properties is prepared and its persistent time can reach more than 1600 min. In the coprecipitation process, a small amount of glucose operates to refe the luminescent powders. The particle size of the phosphor can be less than 1 μm. The sintering temperature of the sample prepared by the coprecipitation method is much lower than that of the one prepared by the high temperature solid state method.Compared with the high temperature solid state method, a clear blue shift occurs in the excitation and emission spectra of the samples.
参考文献
| [1] | Mastsuzama T;Aoki Y;Takeuchi N et al.A new long phosphorescent phosphor with high brightness, SrAl2O4:Eu2+ , Dy3+[J].Journal of the Electrochemical Society,1996,143(08):2670. |
| [2] | Yamamoto H;Matsuzawa T .Mechanism of long phosphorescence of SrAl2O4:Eu2+, Dy3+ and CaAl2O4:Eu2+, Nd3+[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,1997(0):287-289. |
| [3] | Nakazawa E;Mochida T .Traps in SrAl2O4:Eu2+ phosphor with rare-earth ion doping[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,1997(0):236-237. |
| [4] | Mastsuzama T;Nabae T;Sasajima K et al.Effects of composition on the long phosphorescent SrAl2 O4: Eu2 + ,Dy3+ phosphor crystals[J].Journal of the Electrochemical Society,1997,144(09):L243. |
| [5] | Katsumata T.;Nabae T.;Komuro S.;Morikawa T.;Sasajima K. .Characteristics of strontium aluminate crystals used for long-duration phosphors[J].Journal of the American Ceramic Society,1998(2):413-416. |
| [6] | Kato K;Tsutai I;Kamimura T et al.Thermoluminescence properties of SrAl2 O4:Eu sputtered films with long phosphorescence[J].Journal of Luminescence,1999,82:213. |
| [7] | 邱关明,孙彦彬,陈永杰,张明.Studies on Self-Luminous Material and Coating with Long Persistent Yellow-Green Afterglow[J].稀土学报(英文版),2003(05):533-537. |
| [8] | Tang Zilong;Zhang Feng;Zhang Zhongtai et al.Luminescent properties of SrAl2O4: Eu, Dy material prepared by the gel method[J].Journal of the European Ceramic Society,2000,20:2129. |
| [9] | Aitasalo Tuomas;Holsa Jorma;Jungner Hogne.Sol-gel processed Eu2+ -doped alkaline earth aluminates[J].Journal of Alloys and Compounds,2002(341):76. |
| [10] | 袁曦明,许永胜,于江波,王红梅,余启钰.溶胶-凝胶法制备铝酸锶发光材料[J].材料开发与应用,2002(05):26-29. |
| [11] | 熊煜虹,王东,陆毅青,李永祥,殷庆瑞.无机盐溶胶-凝胶工艺制备长余辉发光粉体的研究[J].无机材料学报,2003(02):451-456. |
| [12] | LinYuanhua;Zhang Zhongtai;Zhang Feng .Preparation of the ultrafine SrAl2O4: Eu, Dy needle-like phosphor and its optical properties[J].Materials Chemistry and Physics,2000,65:103. |
| [13] | 李晓云,陆天长,梁爽.铝酸锶系长余辉发光粉的制备及其光学性能[J].南京化工大学学报(自然科学版),2001(02):32-35. |
| [14] | 袁曦明,田熙科,于江波,许永胜.共沉淀法制备长余辉发光材料SrAl2O4：Eu2+,Dy3+的研究[J].材料开发与应用,2002(02):26-30. |
| [15] | Qiu Guanming;Geng Xiujuan;Chen Yongjie et al.Optical property and soft chemical preparation methods of manoscale rare earth luminescent materials[J].中国稀土学报,2003,21(02):109. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%