采用熔融共混挤出法制备纳米氢氧化铝(ATH)为主体的阻燃乙烯-醋酸乙烯共聚物(EVA)材料,研究了阻燃增效剂纳米有机蒙脱土(OMMT)与硼酸锌(ZnB)对复合材料阻燃、力学与电学性能的影响.TEM、TG与FT-IR检测表明,OMMT在基体中插层状分散,不仅提高了材料的拉伸强度,而且在燃烧过程中具有显著的促进基体成炭作用;少量ZnB的加入有效制止了阴燃,此时材料综合性能达到使用要求.
参考文献
[1] | Reiner S .[J].Plastics Additives and Compounding,2002,12:22. |
[2] | Qu B J .[J].Polymer Degradation and Stability,2003,81:401. |
[3] | Hippi U;Mattila J;Korhonen M et al.[J].Polymer,2003,44:1193-1201. |
[4] | Giinter B .[J].Plastics Additives and Compounding,2002,10:22. |
[5] | Wang J Q;Du J X;Zhu J et al.[J].Polymer Degradation and Stability,2002,77:249. |
[6] | Carpentier F.;Le Bras M.;Delobel R.;Foulon M.;Bourbigot S. .Charring of fire retarded ethylene vinyl acetate copolymer - magnesium hydroxide/zinc borate formulations[J].Polymer Degradation and Stability,2000(1):83-92. |
[7] | 郝向阳,刘吉平,冯顺山.蒙脱土与阻燃剂的协效作用[J].高分子材料科学与工程,2003(05):123-126. |
[8] | Hull T;Price D;Liu Y et al.[J].Polymer Degradation and Stability,2003,82:365. |
[9] | Gibert J;Lopez J;Bergeret A et al.[J].Polymer Degradation and Stability,2000,67:440. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%