分别试验了LF2铝合金搅拌摩擦焊焊接接头与氩弧焊接接头的摩擦磨损行为,试验分为3个阶段进行,转数分别为480,1200,2400转.结果表明在相同的实验条件下,搅拌摩擦焊接头的摩擦磨损性能明显优于氩弧焊接接头,其中第一阶段磨损失质量差别不大,后两个阶段搅拌氩弧焊接接头的磨损失质量是搅拌摩擦焊接头的4～6倍.氩弧焊接接头磨损表面呈现明显的塑性变形和表层剥落开裂迹象.搅拌摩擦焊接头磨损表面呈现轻微的疲劳磨损特征.
参考文献
| [1] | 宋刚,刘黎明,王继锋,许德胜.变形镁合金AZ31B的激光焊接工艺研究[J].应用激光,2003(06):327-329,326. |
| [2] | Jin Haiou et al.[J].Materials Science Forum,2000,331-337:1725. |
| [3] | Reynolds A P.[A].Switzerland:Trans Tech Publications Inc,2000:331. |
| [4] | Flores O V et al.[J].Scripta Materialia,1998,38(05):703. |
| [5] | Lienert T J.Hot Deformation of Aluminum Alloys[M].Great Britain,1998:159. |
| [6] | Oertelt G et al.[J].Welding Journal,2001,89(03):71. |
| [7] | Jata K.V.;Semiatin S.L. .Continuous dynamic recrystallization during friction stir welding of high strength aluminum alloys[J].Scripta materialia,2000(8):743-749. |
| [8] | 王快社;王训宏 et al.[J].稀有金属材料与工程,2005,34(09):156. |
| [9] | Miles M P et al.[J].Metallurgical and Materials Transactions,2004,35(11A):3461. |
| [10] | Peel M et al.[J].Acta Materialia,2003,51:4791. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%