采用共溅射方法在玻璃基片上制备了(FePt)1-xCux合金薄膜,FePt合金中添加Cu可以有效降低退火温度,(FePt)1-xCux(x=19.5%)在350℃退火后可以使面内矫顽力Hc∥达到200 kA/m,垂直矫顽力hc⊥达到280 kA/m左右,而纯FePt仅有几千A/m.X射线衍射结果表明退火后形成的FePtCu三元合金是降低退火温度的主要原因.剩磁曲线分析表明Cu的加入不能明显降低晶粒间交换耦合作用.(FePt)1-xCux在400℃退火可以得到10-24m3的磁激活体积.
参考文献
| [1] | 李国栋.2000年～2001年磁性功能材料研究和应用新进展[J].稀有金属材料与工程,2002(06):449-451. |
| [2] | Weller D.;Folks L.;Best ME.;Lee W.;Toney MF.;Schwickert M. Thiele JU.;Doerner MF.;Moser A. .High K-u materials approach to 100 Gbits/in(2)[J].IEEE Transactions on Magnetics,2000(1 Pt.1):10-15. |
| [3] | Thiele JU.;Toney MF.;Weller DK.;Folks L. .Perpendicular magnetic anisotropy and magnetic domain structure in sputtered epitaxial FePt (001) L1(0) films[J].Journal of Applied Physics,1998(10):5686-5692. |
| [4] | 王亦忠,张茂才,乔档,韩宝善,张臻蓉,梁冰青,王荫君,沈保根.各向同性富铁Fe-Pt纳米晶薄膜的形成及其磁性[J].稀有金属材料与工程,2002(03):213-216. |
| [5] | Kuo C M;Kuo P C;Wu H C et al.[J].Journal of Applied Physiology,1999,85:4886. |
| [6] | Shima T;Moriguchi T;Mitani S et al.[J].IEEE Transactions on Magnetics,2002,38:2791. |
| [7] | Xu X H;Wu H S;Wang F et al.[J].Applied Surface Science,2004,233:1. |
| [8] | Platt C L;Wierman K W;Svedberg E B et al.[J].Journal of Applied Physiology,2002,92:6104. |
| [9] | Kitakami O;Shimada Y;Oikawa K et al.[J].Applied Physics Letters,2001,78:1104. |
| [10] | 许小红,武海顺,张富强,金志浩.氮化铝薄膜结构和表面粗糙度的研究[J].稀有金属材料与工程,2000(06):394-397. |
| [11] | 许小红,武海顺,张富强,张聪杰,李佐宜.反应溅射制备AlN薄膜中沉积速率的研究[J].稀有金属材料与工程,2002(03):209-212. |
| [12] | Kai T;Maeda T;Kikitsu A et al.[J].Journal of Applied Physics,2004,95:609. |
| [13] | Bae SY.;Jeong JY.;Kim JG.;Shin KH. .Feasibility of FePt longitudinal recording media for ultrahigh density recording[J].Journal of Applied Physics,2000(9 Pt.3):6953-6955. |
| [14] | Chen SK.;Chin TS.;Tsai JL. .NANOCOMPOSITE SM2CO17/CO PERMANENT MAGNETS BY MECHANICAL ALLOYING[J].Journal of Applied Physics,1996(8 Pt.2b):5964-5966. |
| [15] | Sellmyer D J;Luo C P;Yan M L et al.[J].IEEE Transactions on Magnetics,2001,37:1286. |
| [16] | Shimatsu T;Lodder J C;Sugita Y et al.[J].IEEE Transactions on Magnetics,1999,35:2697. |
| [17] | Witte A M;O'Grady K;Coverdale G N et al.[J].Journal of Magnetism and Magnetic Materials,1990,88:183. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%