Potentiodynamic polarization measurement was used to investigate the effects of temperature, dissolved ox-ygen concentration and pH on the electrochemical behavior of X70 pipeline steel in simulated solution according to the orthogonal testing method. The results showed that temperature, dissolved oxygen concentration and pH had great influence on corrosion current density (icorr)of X70 steel. Corrosion current density of X70 steel was most influenced by dissolved oxygen concentration in simulated solution. The corrosion degree of X70 steel was the least under the environment of low temperature, deficient oxygen and weak acid.
参考文献
| [1] | ZHOU Hua;LI Quan-sheng;ZHU Rui-cheng.Saline Soils' Characteristic of Engineering Geological in Ku'erle,Xinjiang Province[J].West-China Exploration Engineering,2000(03):37. |
| [2] | W. A. Badawy;F. M. Al-Kharafi .Corrosion and passivation behaviors of molybdenum in aqueous solutions of different pH[J].Electrochimica Acta,1998(4):693-702. |
| [3] | M. M. Stack;N. Pungwiwat .Particulate erosion-corrosion of Al in aqueous conditions: some perspectives on pH effects on the erosion-corrosion map[J].Tribology International,2002(10):651-660. |
| [4] | Georgi Ilincev;Dalibor Karnik;Martin Paulovic;Alena Doubkova .The effect of temperature and oxygen content on the flowing liquid metal corrosion of structural steels in the Pb-Bi eutectic[J].Nuclear engineering and design,2006(18):1909-1921. |
| [5] | Parkins R N;Beavers J A .Some Effects of Strain Rate on the Transgranular Stress Corrosion Cracking of Territic Steels in Dilute Near-Neutral-pH Solutions[J].Corrosion,2003,59(03):258. |
| [6] | Manfredi C;Otegui J L .Failures by SCC in Buried Pipelines[J].Engineering Failure Analysis,2002,9:495. |
| [7] | J.Q. Wang;A. Atrens .SCC initiation for X65 pipeline steel in the "high" pH carbonate/bicarbonate solution[J].Corrosion Science,2003(10):2199-2217. |
| [8] | R. Chu;W. Chen;S. -H. Wang .Microstructure Dependence of Stress Corrosion Cracking Initiation in X-65 Pipeline Steel Exposed to a Near-Neutral pH Soil Environment[J].Corrosion: The Journal of Science and Engineering,2004(3):275-283. |
| [9] | B. T. Lu;J. L. Luo .Relationship Between Yield Strength and Near-Neutral pH Stress Corrosion Cracking Resistance of Pipeline Steels-An Effect of Microstructure[J].Corrosion: The Journal of Science and Engineering,2006(2):129-140. |
| [10] | W. Chen;F. King;E. Vokes .Characteristics of Near-Neutral-pH Stress Corrosion Cracks in an X-65 Pipeline[J].Corrosion: The Journal of Science and Engineering,2002(3):267-275. |
| [11] | 杨武.埋地油气管线应力腐蚀破裂研究的一些新进展[J].腐蚀与防护,2003(11):461-467. |
| [12] | FANG Bing-yan;WANG Jian-qiu;ZHU Zi-yong et al.The Stress Corrosion Cracking of Buried Pipelines in Near-NeutralpH and High-pH Solutions[J].Acta Metallrugica Sinica,2001,37(05):452. |
| [13] | 金名惠,孟厦兰,黄辉桃,杜桂焕.碳钢在我国四种土壤中腐蚀机理的研究[J].华中科技大学学报(自然科学版),2002(07):104-107. |
| [14] | Shanghai Science and Technology Communication Station.Designing Methods for Orthogonal Testing--Methods for Numerous Factors[M].上海:上海人民出版社,1975 |
| [15] | The Writers of Orthogonal Testing Method.Orthogonal Testing Method[M].北京:国防工业出版社,1976 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%