结晶器振动导致初凝坯壳受力和变形是产生铸坯表面裂纹的主要原因.通过计算2.0 m/min拉速时弯月面区最大液体摩擦力和最大渣道动态压力,分析了高拉速下结晶器振动参数变化对板坯表面纵裂纹和横裂纹形成的影响,并结合振动参数对结晶器润滑和振动状态的影响,阐明减少表面裂纹的振动参数控制措施.研究结果表明:提高振频和振幅均增大铸坯表面裂纹形成的可能,振频影响强于振幅;增大非正弦振动因子降低了坯壳撕裂可能性,且对润滑有利,但使振痕加深,振动冲击加剧;适当降低振频,增大振幅和非正弦振动因子可抑制表面裂纹形成.
参考文献
| [1] | 蔡开科.连续铸钢[M].北京:科学出版社,1991 |
| [2] | 李宪奎;张德明.连铸结晶器振动技术[M].北京:冶金工业出版社,2000 |
| [3] | 姚曼,王文华,方大成.连铸结晶器与铸坯间保护渣润滑行为的研究[J].钢铁,2001(03):26-29. |
| [4] | 孟祥宁,朱苗勇,程乃良.高拉速下连铸坯振痕形成机理及振动参数优化[J].金属学报,2007(08):839-846. |
| [5] | 孟祥宁,朱苗勇.连铸结晶器非正弦振动波形构造及参数研究[J].中国机械工程,2007(15):1779-1782. |
| [6] | T. Kajitani;K. Okazawa;W. Yamada .Cold model experiment on infiltration of mould flux in continuous casting of steel: Simulation of mould oscillation[J].ISIJ International,2006(10):1432-1441. |
| [7] | Ya MENG;Brian G. THOMAS .Simulation of Microstructure and Behavior of Interfacial Mold Slag Layers in Continuous Casting of Steel[J].ISIJ International,2006(5):660-669. |
| [8] | Ho-Jung SHIN;Seon-Hyo KIM;Brian G. THOMAS .Measurement and Prediction of Lubrication, Powder Consumption, and Oscillation Mark Profiles in Ultra-low Carbon Steel Slabs[J].ISIJ International,2006(11):1635-1644. |
| [9] | Kwon O D;Choi J;Lee I R.Optimization of Mold Oscillation Pattern for the Improvement of Surface Quality and Lubrication in Slab Continuous Casting[A].Washington D.C.:Iron and Steel Society of AIME,1991:561. |
| [10] | 张洪波;王海之 .连铸结晶器振动参数与保护渣物化性能的关系[J].钢铁,1995,30(11):17. |
| [11] | 杨红普,李宪奎,张兴中,金涛.结晶器非正弦振动谐波共振[J].机械工程学报,2007(07):207-212. |
| [12] | 刘宏昭,王建平,原大宁,迟凤志,闫瑞河.连铸机振动系统动态性能分析及其谐振现象研究[J].机械工程学报,2002(03):79-82. |
| [13] | 孟祥宁,朱苗勇,刘旭东,程乃良,江中块.高拉速连铸结晶器非正弦振动因子研究[J].金属学报,2007(02):205-210. |
| [14] | J.W.Cho .Heat Transfer across Mold Flux Film in Mold during Initial Solidification in Continuous Casting of Steel[J].ISIJ International,1998(8):834-842. |
| [15] | Kensuke OKAZAWA;Toshiyuki KAJITANI;Wataru YAMADA;Hideaki YAMAMURA .Infiltration Phenomena of Molten Powder in Continuous Casting Derived from Analysis Using Reynolds Equation Part 1: Steady Analysis[J].ISIJ International,2006(2):226-233. |
| [16] | Ikuhiro SUMI;Hiroshi SHIMIZU;Shinichi NISHIOKA .Initial Solidification Control of Continuous Casting Using Electromagnetic Oscillation Method[J].ISIJ International,2003(6):807-812. |
| [17] | 孟祥宁,朱苗勇.高拉速连铸结晶器非正弦振动同步控制模型[J].钢铁研究学报,2007(07):19-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%