针对铺设在直流电气化铁路附近埋地油气管道管地电位过度负偏移的问题,研究了土壤直流杂散电流对管道的干扰机理以及管道防腐蚀涂层阴极剥离的形成原因,提出了一种管道与接地极(如扁钢、铜、锌带等)之间快速通断的方法,设计了抑制管地电位过度负偏移应用系统.现场测量结果表明,该系统可将管地电位钳制在预先设置的电位附近,有效抑制了管地电位过度负偏移现象,整机系统工作电流仅30 mA.
参考文献
| [1] | 毕方晓,李伟华,傅寿荣,郑海兵,徐志鹏.埋地管道阴极保护电位准则及电位测试方法[J].材料保护,2014(04):72-75. |
| [2] | Chen Zhiguang;Qin Chaokui;Tang Jixu;Zhou Yu .Analyzing of Stray Current Interference on Buried Gas Pipeline from Shanghai Urban Rail Transit[J].Research journal of applied science, engineering and technology,2013(17):4421-4426. |
| [3] | 赵增元,王佳.有机涂层阴极剥离作用研究进展[J].中国腐蚀与防护学报,2008(02):116-120. |
| [4] | 熊娟,张婷,许红川,龚敏,张文艳.埋地管道防腐蚀层阴极剥离影响因素[J].腐蚀与防护,2013(01):60-63. |
| [5] | Effect of cathodic protection on corrosion of pipeline steel under disbonded coating[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(9):2242. |
| [6] | 姚竟迪,梁成浩,黄乃宝,吴建华.有机涂层耐阴极剥离的影响因素研究进展[J].表面技术,2014(03):137-143,151. |
| [7] | Chan Li,Bei Cao,Yinshun Wu.An electrochemical method for evaluating the resistance to cathodic disbondment of anti-corrosion coatings on buried pipelines[J].北京科技大学学报（英文版）,2007(05):414-419. |
| [8] | 陈志光,秦朝葵,计雪松.上海轨道交通二号线杂散电流测试分析[J].腐蚀与防护,2008(06):344-347. |
| [9] | 王新华,刘菊银,何仁洋,陈振华.轨道交通动态杂散电流对埋地管道的干扰腐蚀试验[J].腐蚀与防护,2010(03):193-197. |
| [10] | 吴广春,杜艳霞,路民旭,唐德志,姜子涛.埋地管道交流干扰缓解技术研究现状[J].腐蚀科学与防护技术,2014(05):464-468. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%