By the increase in Mo content, the addition of microalloying elements V and Nb and by reducing the contents of Mn, P and S based on the composition of steel 42CrMo, we have developed a 1300 MPa-grade high strength steel (ADF1) for bolts. The sustained load bending test, sustained load tensile test and stress corrosion cracking test have been carried out to evaluate the delayed fracture resistance of steel ADF1 and commercial steel 42CrMo. The results showed that steel ADF1 has superior delayed fracture resistance to that of 42CrMo steel. It's concluded that the superior delayed fracture resistance of ADF1 is mainly due to the increase of tempering temperature, fine homogeneously distributed MC carbide and fine prior austenite grain size.
参考文献
| [1] | 惠卫军,董瀚,翁宇庆.耐延迟断裂高强度螺栓钢的研究开发[J].钢铁,2001(03):69-73. |
| [2] | Nakasato F;Takahashi M.Delayed-Failure Analysis of High-Strength Structural Bolts[J].Metals and Technology,1980(11):449-455. |
| [3] | Matsuyama S .Delayed Fracture of High Strength Steels[J].Iron and Steel,1994,80(09):679-684. |
| [4] | Pressouyre G M;Bernstein I M .A Quantitative Analysis of Hydrogen Trapping[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1978,9(09):1571-1578. |
| [5] | Hirth J P .Effects of Hydrogen on the Properties of Iron and Steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1980,11:861-890. |
| [6] | Li G F;Wu R G;Lei T C .Carbide-Matrix Interface Mechanism of Stress Corrosion Behavior of High-Strength CrMo Steels[J].Metallurgical and Materials Transactions,1992,23(10):2879-2885. |
| [7] | CHU Wu-yang.Hydrogen Damage and Delayed Fracture[M].北京:冶金工业出版社,1988 |
| [8] | Matsuyama S.Delayed Fracture[M].TOKYO:NIPPON Industry Press,1989 |
| [9] | BANERJI S K;McMahon Jr·C J;Feng H C .Intergranular Fracture in 4340-Type Steels:Effects of Impurities and Hydrogen[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1978,9(02):237-247. |
| [10] | Lin T L;Lan Y;Wu J S .Influence of Austenitizing Temperature on Stress Corrosion in 4330M Steel -The Role of Impurity Segregation in Stress Corrosion Cracking of High Strength Steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1988,19:2225-2231. |