利用区熔定向凝固设备制备了Tb0.3Dy0.7Fe1.95合金,研究了不同定向凝固生长速度下Tb0.3Dy0.7Fe1.95合金的轴向择优取向、晶体的生长方式、结晶形貌的变化规律以及它们之间的关系.结果表明,随着定向凝固生长速度V从低速10μm/s逐步增大到380μm/s,Tb0.3Dy0.7Fe1.95合金的轴向择优取向从<110>方向转变为<311>及<110>、<211>、<533>多种混合轴向取向,之后又转变为原来的<110>方向,当V≥350μm/s后,轴向择优取向变得不明显.在整个过程中出现了2个不稳定过渡阶段,即180μm/s

参考文献

[1] Clark A E.Magnetostrictive rare earth-Fe2 compounds[A].Amsterdam:North-Holland Publishing Company,1980:531.
[2] 王博文.磁致伸缩材料与器件[M].北京:冶金工业出版社,2008:23.
[3] Clark A E.Ferromagnetic Materials Vol.1[M].Amsterdam:North-Holland Publishing Company,1980:591.
[4] Mithun Palit;J. Arout Chelvane;S. Pandian .Effect of solidification rate on the microstructural features and magnetostriction of directionally solidified Tb_(0.3)Dy_(0.7)Fe_(1.95)[J].Scripta materialia,2008(10):819-821.
[5] 周美政,季诚昌,朱世根.TbDyFe合金的定向凝固和取向生长[J].科技导报,2007(04):35-38.
[6] 季诚昌,李建国,马伟增,周尧和.稀土超磁致伸缩材料取向生长和控制[J].材料导报,2001(10):15-18.
[7] Westwood P;Abell J S .Phase relationships in the Tb-Dy-Fe ternary system[J].Journal of Applied Physics,1990,67(09):998.
[8] 王博文 .R-Fe-Al赝三元系相图及其化合物的结构和磁致伸缩(R=Dy<,0.65>Tb<,0.25>Pr<,0.1>)[D].中国科学院金属研究所,1995.
[9] 胡汉起.金属凝固原理[M].北京:机械工业出版社,2008:128.
[10] Tiller W A;Jackson K A;Rutter J W et al.The redistribution of solute atoms during the solidification of metals[J].Acta Metallurgy,1953,1(04):428.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%