通过植酸活化可提高AZ31镁合金化学镀层的耐蚀性能.采用正交试验优化植酸活化工艺,利用金相显微镜观察了植酸膜的微观形貌,测定了植酸膜在质量分数为3.5％的NaCl溶液中的极化曲线及在化学镀镍液中的开路电位.结果表明,当植酸质量浓度为20 g/L、温度为50 ℃、pH=8时处理25 min,植酸膜具有良好的耐蚀性能,并且能够作为化学镀的活化层.
参考文献
| [1] | Zhao H;Huang ZH;Cui JZ .A new method for electroless Ni-P plating on AZ31 magnesium alloy[J].Surface & Coatings Technology,2007(1):133-139. |
| [2] | C. Gu;J. Lian;G. Li .Electroless Ni-P plating on AZ91D magnesium alloy from a sulfate solution[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2005(1/2):104-109. |
| [3] | 李瑛,余刚,刘跃龙,叶立元,郭小华.镁合金的表面处理及其发展趋势[J].表面技术,2003(02):1-5. |
| [4] | Hui Zhao;Zhanghong Huang;Jianzhong Cui .Electroless plating of copper on AZ31 magnesium alloy substrates[J].Microelectronic engineering,2008(2):253-258. |
| [5] | 杨黎晖,李峻青,姜巍巍,张密林.镁合金表面处理技术的研究进展[J].中国腐蚀与防护学报,2008(05):316-320. |
| [6] | XIANG Y H;HU W B;LIU X K et al.Initial deposition mechanism of electroless nickel plating on magnesium alloys[J].Transactions of the Institute of Metal Finishing,2001,79(01):30-32. |
| [7] | 毕虎才,卫英慧,侯利锋,余春燕,胡兰青,许并社.压铸镁合金化学镀Ni-P的沉积过程[J].稀有金属材料与工程,2006(10):1661-1664. |
| [8] | 徐群杰,万宗跃,费琳,印仁和,周小金.植酸自组装膜对白铜缓蚀作用的光电化学研究[J].腐蚀科学与防护技术,2009(02):167-169. |
| [9] | 郑润芬,梁成浩,邵林.AZ91D镁合金植酸转化膜组成与耐蚀性能研究[J].大连理工大学学报,2006(01):16-19. |
| [10] | 崔秀芳,李庆芬.镁合金表面植酸转化膜研究Ⅱ.pH值对镁合金植酸转化膜的影响[J].腐蚀科学与防护技术,2007(04):275-277. |
| [11] | 张华云,刘治国.工艺参数对镁合金植酸转化膜的影响[J].材料保护,2009(08):46-50. |
| [12] | 陈东初,吴建峰,龚伟慧,李文芳,徐东明.AZ91D镁合金表面植酸转化膜的正交实验优化研究[J].兵器材料科学与工程,2009(02):4-8. |
| [13] | 周章添.pH值对镁表面植酸转化膜组织与耐蚀性能的影响[J].热加工工艺,2010(16):114-116. |
| [14] | 崔秀芳,李庆芬.镁合金表面植酸转化膜研究Ⅰ植酸转化膜成膜机理与耐蚀性研究[J].腐蚀科学与防护技术,2007(03):203-206. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%