用熔融缩聚法合成了一系列聚(丁二酸丁二醇酯丁二酸环己烷二甲醇酯)的无规共聚物.用FT-IR,~1H-NMR,DSC,TGA,XRD及水降解测试等方法表征了材料的结构与性能.通过DSC和TGA分析得到产物的熔点虽然较聚丁二酸丁二醇酯(PBS)有所降低,但是热分解温度却得到了提高;XRd测试结果表明,共聚物的晶体结构并没有发生改变;水降解测试结果表明,共聚物较PBS的降解速率有所提高.
A series of copolyesters of succinic acid-1,4-butanediol/succinic acid-1,4-cycl- ohexanedimethanol were synthesized and characterized by means of Fourier transform infrared spectroscopic(FT-IR), hydrogen nuclear magnetic resonance spectrum (~1H-NMR), differential scanning calorimetry ( DSC), thermogravimetry analysis (TGA), X-ray diffraction (XRD) and hydrolytic degradation. Though the melting temperature decreased, the copolymers showed the higher thermal decomposition temperature which was justified by TGA. X-ray diffraction shows that the crystal structure of copolymers is the same as poly (butylene succinate) (PBS). The results of hydrolytic degradation show that the rate of biodegradation of copolymers are higher than that of PBS.
参考文献
| [1] | Fujimaki T. .Processability and properties of aliphatic polyesters, 'BIONOLLE', synthesized by polycondensation reaction[J].Polymer Degradation and Stability,1998(1/3):209-214. |
| [2] | 孙杰,张大伦,谭惠民,罗运军.聚丁二酸丁二醇酯的共聚改性[J].中国塑料,2004(01):43-45. |
| [3] | Cao A.;Okamura T.;Ishiguro C.;Nakayama K.;Inoue Y.;Masuda T. .Studies on syntheses and physical characterization of biodegradable aliphatic poly(butylene succinate-co-epsilon-caprolactone)s[J].Polymer: The International Journal for the Science and Technology of Polymers,2002(3):671-679. |
| [4] | Du J;Zheng YB;Chang J;Xu LA .Synthesis, characterization and properties of high molecular weight poly(butylenes succinate) reinforced by mesogenic units[J].European Polymer Journal,2007(5):1969-1977. |
| [5] | V. Tserki;P. Matzinos;E. Pavlidou;D. Vachliotis;C. Panayiotou .Biodegradable aliphatic polyesters. Part Ⅰ. Properties and biodegradation of poly(butylene succinate-co-butylene adipate)[J].Polymer Degradation and Stability,2006(2):367-376. |
| [6] | Ihn KJ.;Im SS.;Yoo ES. .STRUCTURE AND MORPHOLOGY OF POLY(TETRAMETHYLENE SUCCINATE) CRYSTALS[J].Macromolecules,1995(7):2460-2464. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%