利用旋转涂布法在镁合金表面构建了由聚乙烯亚胺(Polyethyleneimine,PEI)、明胶(Gelatin,Gel)和硝酸铈(Cerium nitrate)组成的抗腐蚀性铈多层膜.采用接触角测试仪表征了铈多层膜在镁合金表面的组装过程;利用电化学交流阻抗图谱和极化曲线研究了铈多层膜修饰的镁合金在0.14mol/L NaCl溶液中的抗腐蚀性能;以MTT和碱性磷酸酶考察了铈多层膜修饰镁合金的细胞相容性.结果表明,在镁合金表面形成了铈多层膜结构,铈多层膜表面处理提高了镁合金的抗腐蚀性能和细胞相容性.该表面处理为镁合金植入体的应用提供了新思路.
参考文献
| [1] | Zhao M;Wu SS;An P;Luo JR .Study on the deterioration process of a chromium-free conversion coating on AZ91D magnesium alloy in NaCl solution[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(2):468-475. |
| [2] | shi Zhiming;song Guangling et al.Corrosion resistance of anodized single-phase Mg alloys[J].Surface and Coatings Technology,2006,201(1-2):492. |
| [3] | Shi Zhiming;Song Guangling et al.The corrosion perforrrmnce of anodized magnesium alloys[J].Corrosion Science,2006,48(11):3531. |
| [4] | Yfantis A.;Paloumpa I.;Schmeisser D.;Yfantis D. .Novel corrosion-resistant films for Mg alloys[J].Surface & Coatings Technology,2002(0):400-404. |
| [5] | Ghasemi A;Raja VS;Blawert C;Dietzel W;Kainer KU .Study of the structure and corrosion behavior of PEO coatings on AM50 maginesium. alloy by electrochemical impedance spectroscopy[J].Surface & Coatings Technology,2008(15):3513-3518. |
| [6] | Yang, JX;Jiao, YP;Cui, FZ;Lee, IS;Yin, QS;Zhang, Y .Modification of degradation behavior of magnesium alloy by IBAD coating of calcium phosphate[J].Surface & Coatings Technology,2008(22/23):5733-5736. |
| [7] | 邵敏华,黄若双,付燕,胡融刚,林昌健.Al合金表面Ce转化膜成膜机理研究[J].物理化学学报,2002(09):791-795. |
| [8] | 顾宝珊,刘建华,纪晓春.铈盐对铝合金的缓蚀机理研究[J].中国腐蚀与防护学报,2006(01):53-58. |
| [9] | 钟丽应,刘文娟,曹发和,张昭,张鉴清.稀土铈、镧合金化对AZ91腐蚀行为的影响[J].腐蚀科学与防护技术,2009(02):91-93. |
| [10] | 张勇,许越,周德瑞,陈湘,吴正勇,崔国峰.稀土铈对AZ91镁合金表面腐蚀性能的影响[J].哈尔滨工业大学学报,2002(03):376-378. |
| [11] | Zhu H G;Ji J;Tan Q G et al.Surface engineering of poly (DL-lactide)via electrostatic self-assembly of extracellular matrix-like molecules[J].Biomacromolecules,2003,4(02):378. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%