取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布.利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构.结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}＜001＞织构比例最高,而热轧板心部的{100}＜110＞织构比例最低;铜含量对热轧织构中{114}＜110＞和{001}＜100＞织构发展有显著影响.
参考文献
| [1] | 何忠治.电工钢[M].北京:冶金工业出版社,1997 |
| [2] | 赵宇,李军,董浩,孙颖,李波.国外电工钢生产技术发展动向[J].钢铁,2009(10):1-5. |
| [3] | Harase J;Shimizu R.Influence of Annealing Temperature Before Cold Rolling and Cu Content on the Secondary Recrystallization in Nitried Fe-3% Alloy[J].Journal of Magnetism and Magnetic Materials,2003(254/255):343. |
| [4] | Kubota T;Fujikura M;Ushigami Y .Recent Progress and Future Trend on Grain-Oriented Silicon Steel[J].Journal of Magnetism and Magnetic Materials,2000,1(215/216):69. |
| [5] | Dorothee Dorner;Stefan Zaefferer;Ludger Lahn .Overiew of Microstructure and Microtexture Development Grain-oriented Silicon Steel[J].Journal of Magnetism and Magnetic Materials,2006(2):183-186. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%