利用扫描电子显微镜(SEM)、电子能谱(EDS)以及X射线衍射(XRD)技术研究了9Cr低活化马氏体钢在650℃/25MPa超临界水中的腐蚀行为.结果表明,9Cr低活化马氏体钢腐蚀产物的晶粒随腐蚀时间的延长而长大,晶粒尺寸从200h的5.7μm长大到1000h的10.1μm.表面形成的氧化膜为双层结构,外层为Fe3O4,内层由Fe3O4和FeCr2O4共同组成.由氧化增重结果获得了9Cr低活化马氏体钢在超临界水中腐蚀的氧化动力学表达式,同时其腐蚀机理表现为吸氧腐蚀.
参考文献
| [1] | Squarer D;Schulenberg T;Struwe D et al.High performance light water reactor[J].Nuclear Engineering and Design,2003,221(1-3):167. |
| [2] | 朱发文,张乐福,唐睿,乔培鹏,刘瑞芹.奥氏体304NG不锈钢在550℃/25 MPa超临界水中的腐蚀行为[J].原子能科学技术,2009(06):518-522. |
| [3] | 朱发文,张乐福,唐睿,乔培鹏,鲍一晨.铁素体-马氏体钢P92在超临界水中的腐蚀性能[J].原子能科学技术,2010(08):979-983. |
| [4] | Corrosion of nickel-chromium alloys, stainless steel and niobium at supercritical water oxidation conditions[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(1):118. |
| [5] | Corrosion behavior of Hastelloy C-276 in supercritical water[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(9):2092. |
| [6] | Kaiju Yin;Shaoyu Qiu;Rui Tang .Corrosion behavior of ferritic/martensitic steel P92 in supercritical water[J].The Journal of Supercritical Fluids,2009(3):235-239. |
| [7] | J. Isselin;R. Kasada;A. Kimura .Corrosion behaviour of 16%Cr-4%Al and 16%Cr ODS ferritic steels under different metallurgical conditions in a supercritical water environment[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(10):3266-3270. |
| [8] | Progress in corrosion resistant materials for supercritical water reactors[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(11):2508. |
| [9] | Localized corrosion of magnetite on ferritic-martensitic steels exposed to supercritical water[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(11):2503. |
| [10] | Corrosion behavior of 9-12% Cr ferritic-martensitic steels in supercritical water[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(4):1520. |
| [11] | LI Xing-gang,YAN Qing-zhi,MA Rong,WANG Hao-qiang,GE Chang-chun.First Results of Characterization of 9Cr-3WVTiTaN Low Activation Ferritic/Martensitic Steel[J].钢铁研究学报（英文版）,2010(05):57-62. |
| [12] | Was GS;Ampornrat P;Gupta G;Teysseyre S;West EA;Allen TR;Sridharan K;Tan L;Chen Y;Ren X .Corrosion and stress corrosion cracking in supercritical water[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2007(1/3):176-201. |
| [13] | Ren X;Sridharan K;Allen TR .Corrosion of ferritic-martensitic steel HT9 in supercritical water[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2006(2/3):227-234. |
| [14] | Yun Chen;Kumar Sridharan;Todd Allen .Corrosion behavior of ferritic-martensitic steel T91 in supercritical water[J].Corrosion Science,2006,48(09):2843. |
| [15] | Yi Yongsun;Lee Byeonghak;Kim Sungho et al.Corrosion and corrosion fatigue behaviors of 9Cr steel in a supercritical water condition[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2006,429(1-2):161. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%