SrAl2 O4: Eu, Dy nanometer phosphors were synthesized by combustion method at 500 ～ 900℃, followed by heating the combustion sample at 1150℃ at a weak reductive atmosphere and nanometer phosphor with much better luminescent properties was obtained. The influences of the initiating combustion temperature, H3BO3 quantity, the mass ratio of urea and nitrate on the luminescent intensity of nanometer phosphors were studied. The optimum synthetic conditions were determined. The analysis results by transmission electron microscopy (TEM) indicate that the particle size of the synthetic product is less than 75 nm. The luminescent materials do not need to be ground. Their coating can be refined. It supplies a new approach to the rapid preparation of the luminescent materials at low temperature. The excitation and emission spectra indicate that the main peaks in the excitation and emission spectrum of nanometer phosphor synthesized by combustion method shifted to the short wavelength compared with the phosphor obtained by the solidstate reaction synthesis method. The reason of blue shift was explained. The afterglow decay results indicate that the decay speed of the afterglow for nanometer phosphor is faster than that obtained by the solid-state reaction method.
参考文献
| [1] | Liu Shengli;Su Qiang .Sol-gel synthesis and luminescence of Y4A12O9: RE3+ (RE = Eu,Tb)[J].Journal of Alloys and Compounds,1997,255:102. |
| [2] | Kutty T R N;Jagannathan R;Rao R P .Luminescence of Eu2+ in strontium alminates prepared by the hydrothermal method[J].Materials Research Bulletin,1990,25(11):1355. |
| [3] | Kingsley J J;Suresh K;Patil K C .Combustion synthesis of fme-particle metal aluminates[J].Journal of Materials Science,1990,25:1305. |
| [4] | 郑仕远,胡春平.SrAl2O4：Eu2+,Dy3+型发光粉合成新方法[J].新技术新工艺,2000(07):37-38. |
| [5] | 任新光,孟继武.电弧法SrAl2O4：Eu2+长余辉发光陶瓷的制备及其光谱分析[J].光谱学与光谱分析,2000(03):268-269. |
| [6] | Cai Shaohua;Xu Jian;Li Yuanying et al.Study on luminescence of phosphors with long persistence aluminate synthesized by microwave irradiation technique[J].中国稀土学报,1999,17(zk):697. |
| [7] | 邱关明,耿秀娟,陈永杰,孙彦彬,田一光,张明.纳米稀土发光材料的光学特性及软化学制备[J].中国稀土学报,2003(02):109-114. |
| [8] | 邱关明,孙彦彬,陈永杰,张明.Studies on Self-Luminous Material and Coating with Long Persistent Yellow-Green Afterglow[J].稀土学报(英文版),2003(05):533-537. |
| [9] | Lin YH.;Zhang F.;Tang ZL.;Chen QM.;Zhang ZT. .Preparation of the ultrafine SrAl2O4 : Eu,Dy needle-like phosphor and its optical properties[J].Materials Chemistry and Physics,2000(1):103-106. |
| [10] | MATSUZAWA T;Aoki Y;Takeuchi N et al.A new long phosphorescent phosphor with high brightness,SrA12 O4: Eu2 + , Dy3 +[J].Journal of the Electrochemical Society,1996,143(08):670. |
| [11] | JIA W;Yuan H;Lu L et al.Phosphorescent dynamics in SrA12O4:Eu2+,Dy3+ single crystal fibers[J].Journal of Luminescence,1998,76-77:424. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%