利用气体保护钨极氩弧焊(GTAW),采用ER309L和ER308两种焊丝对Q345/316L异种钢进行焊接试验,并利用光学显微镜、扫描电镜、万能试验机、冲击试验机、显微硬度仪等对焊接接头的显微组织结构及力学性能进行研究.结果表明:焊缝金属为奥氏体和铁素体组织,在Q345侧热影响区(HAZ)发现有明显的碳元素迁移现象,焊缝中Cr、Ni等合金元素成分迁移很小,稀释不明显;焊缝-316L交界处形成了宽约50 μm的熔合区.ER309L焊接接头在强度、塑性、冲击韧性和显微硬度方面优于ER308焊接接头;同时,两者拉伸断裂均发生在Q345侧HAZ部位,接头焊缝冲击韧性良好,显微硬度高于两侧母材.

Q345/316L dissimilar steel welding joints were produced by gas tungsten arc welding using two welding wires of ER309L and ER308,respectively.Microstructure and mechanical properties of the welding joints were investigated by means of optical microscope,SEM and EDS analysis,tensile test,impact and hardness tests.The results show that the microstructure of the welding is composed of austenite and ferrite.The diffusion of carbon element is obvious in the heat effected zone (HAZ) of the Q345 steel side,and no significant diffusion of Cr and Ni elements is observed in the welding seam,and no obvious dilution of the element is found.A complex fusion zone with about 50 μm width is formed at the welding-316L steel interface.Compared to ER308 welded joints,the ER309L welded joints exhibit better performance of tensile strength,plasticity,impact toughness and hardness.All the tensile fracture occurs at the HAZ of the Q345 steel side,the impact toughness and the hardness of the welded joints are higher than that of the base materials.

参考文献

[1] 欧平;孙坚;张茂龙;魏一.SA508/316L异种钢焊接接头的显微组织[J].材料热处理学报,2013(10):132-138.
[2] 黄本生;刘阁;刘记;刘清友.时效处理对Q235/316L异种钢焊接头组织及性能的影响[J].材料热处理学报,2013(10):139-145.
[3] 刘俊建;陈国宏;余新海;王家庆;化建;宋有明;张涛;汤文明.T92/HR3C异种钢焊接接头的组织结构和力学性能[J].材料热处理学报,2011(2):54-60.
[4] 王可;郑振太;薛海涛;宋红伟.254SMO/Q235B异种钢焊接接头显微组织[J].焊接学报,2013(2):105-108.
[5] 宋有明;陈国宏;余新海;刘俊建;王家庆;化建;张涛;张建华;汤文明.T92/HR3C异种钢焊接接头高温拉伸变形及断裂行为[J].材料热处理学报,2012(2):72-78.
[6] Jian Cao;Yi Gong;Kai Zhu;Zhen-Guo Yang;Xiao-Ming Luo;Fu-Ming Gu.Microstructure and mechanical properties of dissimilar materials joints between T92 martensitic and S3D4H austenitic steels[J].Materials & design,20115(5):2763-2770.
[7] 黄本生;刘阁;黄龙鹏;刘辉;张怀辉.不同焊材匹配与时效处理对异种钢焊接接头显微结构与力学性能的影响[J].材料工程,2013(8):75-84.
[8] 史春元;李小刚;于启湛;李江华;于泓;于凤;罗洪涛.异种钢焊接接头加热后碳迁移区力学性能的变化规律[J].焊接学报,2000(3):59-61.
[9] 何金光;曾菲圆;雷斌隆;周友龙;钟剑文.022Cr23Ni5Mo3N与Q345B异种钢焊接接头的组织与力学性能分析[J].电焊机,2012(12):104-107.
[10] M.L.Huang L.Wang.Carbon Migration in 5Cr-0.5Mo/21Cr-12Ni Dissimilar Metal Welds[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,199812(12):3037-3046.
[11] Tetsumi Yuri;Toshio Ogata;Masahiro Saito.Effect of welding structure and δ-ferrite on fatigue properties for TIG welded austenitic stainless steels at cryogenic temperatures[J].Cryogenics,20004/5(4/5):251-259.
[12] 黄明亮;王来;亚生江;王富岗;于承志.异质焊头Cr5Mo/Cr21Ni12碳扩散的研究[J].金属学报,2000(9):902-906.
[13] Marashi P;Pouranvari M;Amirabdollahian S;Abedi A;Goodarzi M.Microstructure and failure behavior of dissimilar resistance spot welds between low carbon galvanized and austenitic stainless steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20081/2(1/2):175-180.
[14] N. A. McPherson;K. Chi;M. S. Mclean.Structure and properties of carbon steel to duplex stainless steel submerged arc welds[J].Materials Science and Technology: MST: A publication of the Institute of Metals,20032(2):219-226.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%