采用重稀土Gd和轻稀土Sm代替WE系列中的Y和Nd等稀土元素，设计开发了Mg-Gd-Sm-Zr系高性能镁合金。利用XRD、OM、SEM、EDS及拉伸试验，研究了Mg-12Gd-Sm-0.5Zr合金的微观组织、室温和高温力学特性。结果表明：合金由α-Mg基体、Mg5Gd相和Mg41Sm5相组成；在室温到300℃范围内合金的抗拉强度较稳定，室温抗拉强度为238 MPa，200、250、300℃分别为263、266、256 MPa，合金在该温度范围内具有抗拉强度的温度效应。
The high performance magnesium alloys of Mg-Gd-Sm-Zr series were prepared with heavy rare earth Gd and light rare earth Sm instead of rare earth Y and Nd of WE series respectively. The microstructure and the mechanical behaviors of Mg-12Gd-Sm-0.5Zr alloyat room temperature and high temperature were investigated by XRD,OM,SEM,EDS and tensile test. The results show that the microstructure of the alloy includesα-Mg matrix,and Mg5Gd and Mg41Sm5 phase. The properties of the alloy are stable from room temperature to the high temperature of 300℃,the tensile strength at room temperature is 238 MPa,and the tensile strength of the alloy at 200,250,300℃reaches 263,266,256 MPa respectively. The temperature effect of the tensile strength exists in the alloy within a certain temperature range.
参考文献
| [1] | 陈振华.耐热镁合金[M].北京:化学工业出版社,2007:1-534. |
| [2] | 李大全 .Mg-Y-Sm-Zr系镁合金组织性能研究[D].上海交通大学,2008. |
| [3] | Lidong Wang;Chengyao Xing;Xiuli Hou;Yaoming Wu;Jianfei Sun;Limin Wang .Microstructures and mechanical properties of as-cast Mg–5Y–3Nd–Zr–xGd (x = 0, 2 and 4 wt.%) alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(7/8):1891-1895. |
| [4] | 孙明,吴国华,王玮,侯正全,陈斌,丁文江.Mg-Gd系镁合金的研究进展[J].材料导报,2009(11):98-103. |
| [5] | PENG Qiuming,MA Ning,LI Hui.Gadolinium solubility and precipitate identification in Mg-Gd binary alloy[J].稀土学报（英文版）,2012(10):1064-1068. |
| [6] | PENG Qiuming,MA Ning,LI Hui.Gadolinium solubility and precipitate identification in Mg-Gd binary alloy[J].稀土学报（英文版）,2012(10):1064-1068. |
| [7] | 张清,李全安,井晓天,张兴渊.稀土Sm在耐热镁合金中的应用[J].铸造,2010(03):260-262. |
| [8] | Rokhlin L L.Magnesium alloys containing rare-earth metals[M].London:taylor and Francis,2003:291-296. |
| [9] | 李克杰 .含Sm、Sb耐热镁合金显微组织和性能研究[D].西安:西安理工大学,2010. |
| [10] | 李克杰,李全安.Sm和Sb对时效态Mg-12Gd-2Y-0.5Zr合金组织与力学性能的影响[J].材料热处理学报,2011(05):110-115. |
| [11] | Rokhlin L L;Nikitina N I;Dobatkina T V .Solid-state phase equilibria in the Mg corner of the Mg-Gd-Sm phase diagram[J].Journal Alloys Compound,1996,82(04):113-118. |
| [12] | Peng Qiuming;Hou Xiuli;Wang Lidong et al.Microstructure and mechanical properties of Mg-Gd based alloys[J].Materi-als and Design,2009,30(04):292-296. |
| [13] | P. J. Apps;H. Karimzadeh;J. F. King;G. W. Lorimer .Phase compositions in magnesium-rare earth alloys containing yttrium, gadolinium or dysprosium[J].Scripta materialia,2003(5):475-481. |
| [14] | T. Honma;T. Ohkubo;K. Hono;S. Kamado .Chemistry of nanoscale precipitates in Mg-2.1Gd-0.6Y-0.2Zr (at.%) alloy investigated by the atom probe technique[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):301-306. |
| [15] | C. Antion;P. Donnadieu;F. Perrard;A. Deschamps;C. Tassin;A. Pisch .Hardening precipitation in a Mg-4Y-3RE alloy[J].Acta materialia,2003(18):5335-5348. |
| [16] | 何上明 .Mg-Gd-Y-Zr(-Ca)合金的微观组织演变、性能和断裂行为研究[D].上海交通大学,2007. |
| [17] | Wolfgang Pfeiler.Alloy physics[M].KGaA:Wiley-VCH Ver-lag GmbH&Co,2007:280-330. |
| [18] | 胡耀波,邓娟,赵冲,王敬丰,潘复生.固溶态Mg-Gd-Zr合金的组织与力学性能[J].中国有色金属学报（英文版）,2011(04):732-738. |
| [19] | 丁文江.镁合金科学与技术[M].北京:科学出版社,2007:124-131. |
| [20] | Rokhlin LL.;Nikitina NI. .Recovery after ageing of Mg-Y and Mg-Gd alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1998(2):166-170. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%