Employing Li2CO3, NiO, Co3O4, and MnCO3 powders as starting materials, Li[Ni1/3Co1/3Mn1/3]O2 was synthesized by solid-state reaction method.Various grinding aids were applied during milling in order to optimize the synthesis process.After successive heat treatments at 650 and 950 ℃, the prepared powders were characterized by X-ray diffraction (XRD) analysis, scanning electron microscopy, and transmission electron microscopy.The powders prepared by adding salt (NaCl) as grinding aid exhibit a clear R3m layer structure.The powders by other grinding aids like heptane show some impurity peaks in the XRD pattern.The former powders show a uniform particle size distribution of less than 1 μm average size while the latter shows a wide distribution ranging from 1 to 10 μm.Energy dispersive X-ray (EDX) analysiss show that the ratio of Ni, Co, and Mn content in the powder is approximately 1/3, 1/3, and 1/3, respecively.The EDX data indicate no incorporation of sodium or chlorine into the powders.Charge-discharge tests gave an initial discharge capacity of 160 mAh·g-1 for the powders with NaCl addition while 70 mAh·g-1 for the powders with heptane.
参考文献
[1] | Pasquali M;Passerini S;Pistoia G.[M].Kluwer Academic Publishers,2004:315. |
[2] | Yabuuchi N;Ohzuku T .Novel lithium insertion material of LiCo1/3Ni1/3Mn1/3O2 for advanced lithium-ion batteries[J].Journal of Power Sources,2003,119-121:171. |
[3] | Park SH;Shin SS;Sun YK .The effects of Na doping on performance of layered Li1.1-xNax[Ni0.2Co0.3Mn0.4]O-2 materials for lithium secondary batteries[J].Materials Chemistry and Physics,2006(2/3):218-221. |
[4] | Shin HS;Park SH;Bae YC;Sun YK .Synthesis of Li[Ni0.475Co0.05Mn0.475]O-2 cathode materials via a carbonate process[J].Solid state ionics,2005(35/36):2577-2581. |
[5] | Lee M H;Kang Y J;Myung S T et al.Synthetic optimization of Li[Ni1/3Co1/3Mn1/3]O2 via co-precipitation[J].Electrochimica Acta,2004,50:939. |
[6] | Luo X;Wang X;Liao L et al.Synthesis and characterization of high tap-density layered Li[Ni1/3Co1/3Mn1/3]O2 cathode material via hydroxide co-precipitation[J].Journal of Power Sources,2006,158:654. |
[7] | Park S H;Yoon C S;Kang S G et al.Synthesis and structural characterization of layered Li[Ni1/3Co1/3Mn1/3]O2 cathode materials by ultrasonic spray pyrolysis method[J].Electrochimica Acta,2004,49:557. |
[8] | Jang S B;Kang S H;Amine K et al.Synthesis and improved electrochemical performance of Al(OH)3-coated Li[Ni1/3Mn1/3Co1/3]O2 cathode materials at elevated temperature[J].Electrochimica Acta,2005,50:4168. |
[9] | Yoon C S;Kim C K;Sun Y K .Cycling behavior of selenium-doped LiMn2O4 spinel cathode material at 3 V for lithium secondary batteries[J].Journal of Power Sources,2002,109:234. |
[10] | Lee Y S;Sun Y K;Adachi K et al.Synthesis and electrochemical characterization of orthorhombic LiMnO2 material[J].Electrochimica Acta,2003,48:1031. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%